Friction and wear behaviors of a high nitrogen austenitic stainless steel Fe-19Cr-15Mn-0.66N
نویسندگان
چکیده
The friction and wear behaviors of a Fe-19Cr-15Mn-0.66N high nitrogen austenitic stainless steel (HNSS) were investigated. Tribological investigations carried out under different applied loads 5 N, 10 15 20 N. Scanning electron microscope (SEM) laser scanning confocal (LSCM) used to understand the mechanisms reasons for improved resistance. lower coefficient resistance observed with increase in loads. Under higher load, enhanced work hardening ability HNSS, which turn its surface hardness thus increased HNSS.
منابع مشابه
STUDY THE WEAR MECHANISM OF A PLASMA ELECTROLYTIC NITROCARBURISED (PEN/C) 316L AUSTENITIC STAINLESS STEEL
The wear mechanism of plasma electrolytic nitrocarburised (PEN/C) 316L stainless steel samples was studied after a pin on disc wear test. The surface morphology of samples after application of PEN/C process was studied using scanning electron microscope technique. The sliding tracks resulting from the wear tests on the treated specimens indicated no signs of plastic deformation and adhesive wea...
متن کاملMicrostructure, Mechanical and Corrosion Properties of Friction Stir Welding High Nitrogen Martensitic Stainless Steel 30Cr15Mo1N
High nitrogen martensitic stainless steel 30Cr15Mo1N plates were successfully welded by friction stir welding (FSW) at a tool rotation speed of 300 rpm with a welding speed of 100 mm/min, using W-Re tool. The sound joint with no significant nitrogen loss was successfully produced. Microstructure, mechanical and corrosion properties of an FSW joint were investigated. The results suggest that the...
متن کاملWear and repair of stainless steel crowns.
AIM The purpose of this study was to determine the wear of stainless steel crowns (SSCs) in children, and compare the extent of microleakage in SSCs that had been repaired using either a cermet glass-ionomer cement (GIC) or a packable composite resin (CR). MATERIALS AND METHODS For the first aim, the occlusal surface thickness of 31 harvested SSCs (21 primary first and 10 second molars) and 1...
متن کاملAn evaluation of weld metal nitrogen retention and properties in 316LN austenitic stainless steel
A series of tests were conducted using varying levels of nitrogen and helium in a conventional argon shielding gas when welding 316LN austenitic stainless steel. The outcome was that a 15 per cent nitrogen addition to the argon shielding gas had the most significant effect on increasing the weld metal nitrogen. Subsequent additions of helium to the argon 15 per cent nitrogen shielding gas had v...
متن کاملMicrostructural evolution of 304 austenitic stainless steel in friction stir welding process
Friction stir welding (FSW) was conducted on AISI 304 austenitic stainless steel plate with 2 mm thickness. The FSW was performed at a welding and rotational speeds of 50 mm/min and 400 rpm, respectively. Microstructure observations by the optical microscopy showed that a severe grain refinement occurred in the stir zone (SZ). Electron backscattered diffraction analysis (EBSD) results indicated...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Mining and Metallurgy, Section B
سال: 2021
ISSN: ['1450-5339', '2217-7175']
DOI: https://doi.org/10.2298/jmmb201026025q