Fretting Fatigue Researches and Design Curve
نویسندگان
چکیده
منابع مشابه
Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy
An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scann...
متن کاملA ‘crack-like’ notch analogue for a safe-life fretting fatigue design methodology
A B S T R A C T Various analogies have recently been proposed for comparing the stress fields induced in fretting fatigue contact situations, with those of a crack and a sharp or a rounded notch, resulting in a degree of uncertainty over which model is most appropriate in a given situation. However, a simple recent approach of Atzori–Lazzarin for infinite-life fatigue design in the presence of ...
متن کاملFretting Fatigue Life Estimations Based on Critical Distance Theory
Fretting fatigue process have many features such as early stage crack initiation at contact edge, very slow crack propagation and fatigue failure after very long life operation. In this paper at first we present fretting fatigue model in high cycle region, which is considering the wear process near contact edge. And then we present fretting fatigue life estimation method in low cycle fatigue re...
متن کاملOn the Convergence of Stresses in Fretting Fatigue
Fretting is a phenomenon that occurs at the contacts of surfaces that are subjected to oscillatory relative movement of small amplitudes. Depending on service conditions, fretting may significantly reduce the service life of a component due to fretting fatigue. In this regard, the analysis of stresses at contact is of great importance for predicting the lifetime of components. However, due to t...
متن کاملFretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life
Fretting fatigue experiments and finite element analysis were carried out to investigate the influence of cylindrical-on-flat contact on crack nucleation, crack path and fatigue life of medium-carbon steel. The location of crack nucleation was predicted using the maximum shear stress range criterion and the maximum relative slip amplitude criterion. The prediction using the maximum relative sli...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Marine Engineering
سال: 2009
ISSN: 1346-1427,1884-3778
DOI: 10.5988/jime.44.750