Fracture Toughness of TiAl Intermetallic Compound Prepared by Reactive-Sintering
نویسندگان
چکیده
منابع مشابه
Reactive Sintering of TiAl - Ti 5 Si 3 Lnsitu Composites
TiAl with between 0 and 20 volume percent (v%)Ti5Si3 was produced by reactive sintering of cofd pressed compacts of elemental Ti, Al and Si powder mixtures at 7OO0C for 15 minutes in vacuum. The results show that adding Si to Ti and A1 reduces the swelling associated with reactive sintering of TiAI, as composites containing more than 5 vYoTigSi3 densified during reactive sintering. However, com...
متن کاملAN INVESTIGATION ON REACTIVE SINTERING OF NANO-CRYSTALLINE TiO2 -Al POWDER PREPARED BY MECHANICAL ALLOYING
In this research an ultra-fine grained composite structure consisting of an intermetallic matrix together with dispersed nano-sized Al2O3 obtained via mechanical activation of TiO2 and Al in a high energy ball mill and sintering of consolidated samples. Phase composition and morphology of the milled and sintered samples were evaluated by XRD and SEM techniques Thermal behavior of the powder sa...
متن کاملHIGH-TEMPERATURE FRACTURE AND FATIGUE RESISTANCE OF A DUCTILE b-TiNb REINFORCED g-TiAl INTERMETALLIC COMPOSITE
ÐThe high-temperature fatigue-crack propagation and fracture resistance of a model g-TiAl intermetallic composite reinforced with 20 vol.% ductile b-TiNb particles is examined at elevated temperatures of 650 and 8008C and compared with behavior at room temperature. TiNb reinforcements are found to enhance the fracture toughness of g-TiAl, even at high temperatures, from about 12 to 040 MPa m, a...
متن کاملX-ray Stress Measurement for Ni-Al System Intermetallic Compound Prepared by SHS- method
An X-ray diffraction technique was used to measure the residual stress in the surface of a specimen containing a coating of a NijAl intermetallic compound produced bythe SHS (Self-propagation High temperature Synthesis) method. The Ni3Al was using the coating material for spherical carbon cast iron substrate and austenite stainless steel substrate. Differences between the coefftcient of thermal...
متن کاملStrength and Toughness of Ceramic-metal Prepared by Reactive Hot Pressing Composites
William G. Fahrenholtz o 9m Ceramic Engineering Department ‘so University of Missouri-Rolls w~!!l Rolls, MO 65409 + <. +# Metal-reinforced Alz03-matrix composites were prepared using reactive hot pressing. The volume fraction of the reinforcing phase was controlled by the stoichiometry of the particular displacement reaction used. Dense Alz03-Ni and Al@3-N’b composites were fabricated using thi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1992
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.56.3_342