Fracture toughness of sintered alloy steel compacts.
نویسندگان
چکیده
منابع مشابه
Shape effect of ultrafine-grained structure on static fracture toughness in low-alloy steel.
A 0.4C-2Si-1Cr-1Mo steel with an ultrafine elongated grain (UFEG) structure and an ultrafine equiaxed grain (UFG) structure was fabricated by multipass caliber rolling at 773 K and subsequent annealing at 973 K. A static three-point bending test was conducted at ambient temperature and at 77 K. The strength-toughness balance of the developed steels was markedly better than that of conventionall...
متن کاملFracture toughness of yttrium stabilized zirconia sintered in conventional and microwave ovens
Recommended Citation Marinis, Aristotelis. "Fracture toughness of yttrium stabilized zirconia sintered in conventional and microwave ovens. ii To my sister iii When you set out on your journey to Ithaca, pray that the road is long, full of adventure, full of knowledge. iv ACKNOWLEDGMENTS First and foremost I would like to express my sincere gratitude to my thesis supervisor Dr. Steven A. Aquili...
متن کاملFracture toughness of yttria-stabilized zirconia sintered in conventional and microwave ovens.
STATEMENT OF PROBLEM The fabrication of zirconium dioxide (ZrO2) dental prosthetic substructures requires an extended sintering process (8 to 10 hours) in a conventional oven. Microwave sintering is a shorter process (2 hours) than conventional sintering. PURPOSE The purpose of this study was to compare the fracture toughness of 3 mol % Y2O3-stabilized ZrO2 sintered in a conventional or micro...
متن کاملFracture toughness of graphene.
Perfect graphene is believed to be the strongest material. However, the useful strength of large-area graphene with engineering relevance is usually determined by its fracture toughness, rather than the intrinsic strength that governs a uniform breaking of atomic bonds in perfect graphene. To date, the fracture toughness of graphene has not been measured. Here we report an in situ tensile testi...
متن کاملEffect of Microstructural Variations on the Fracture Toughness of Wrought Alloy 718
The effect of microstructural variations on the fracture toughness of Alloy 718 was reviewed. The metallurgical parameters surveyed in this paper included heat treatment, heat-to-heat variations, product-form variations, neutron irradiation and long-term thermal aging. Key microstructural features and operative fracture mechanisms were related to macroscopic fracture toughness properties.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1989
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.36.222