Fracture toughness evaluation in sintered high speed steel.
نویسندگان
چکیده
منابع مشابه
Carbide Structure and Fracture Toughness of High Speed Tool Steels
In the present study, M2 high speed steels were fabricated by using electro-slag rapid remelting process. Carbide structure was analysed and the fracture toughness and hardness were also measured after austenitization treatment at 1190 and 1210C followed by tempering treatment at 535C for billets with various diameters from 16 to 60 mm. Electro-slag rapid remelting (ESRR) process is an advanced...
متن کاملDynamic Fracture Toughness versus Crack Tip Speed Relationship at Lower than Room Temperature for High Strength 3239var Structural Steel
A transient _nite element analysis is carried out to provide insight into the low temperature dynamic material toughness versus crack tip relationship for high strength structural steels under intense stress pulse loading[ The problem analyzed here is plane strain fracture of an edge cracked specimen under plane wave loading conditions[ The _nite element formulation employed accounts for the e}...
متن کاملEvaluation of Cleavage Fracture Toughness for Steel by Chevron-Notched Specimen
Fracture toughness tests were conducted for an A533B-1 steel by using chevron-notched compact specimens in the temperature range from the lower shelf regime up to the transition temperature in order to assess the R-curve for cleavage fracture. The applicability of these specimens to the simple fracture toughness test without introducing fatigue pre-cracks was examind. The following are the summ...
متن کاملFracture toughness of yttrium stabilized zirconia sintered in conventional and microwave ovens
Recommended Citation Marinis, Aristotelis. "Fracture toughness of yttrium stabilized zirconia sintered in conventional and microwave ovens. ii To my sister iii When you set out on your journey to Ithaca, pray that the road is long, full of adventure, full of knowledge. iv ACKNOWLEDGMENTS First and foremost I would like to express my sincere gratitude to my thesis supervisor Dr. Steven A. Aquili...
متن کاملFracture toughness of yttria-stabilized zirconia sintered in conventional and microwave ovens.
STATEMENT OF PROBLEM The fabrication of zirconium dioxide (ZrO2) dental prosthetic substructures requires an extended sintering process (8 to 10 hours) in a conventional oven. Microwave sintering is a shorter process (2 hours) than conventional sintering. PURPOSE The purpose of this study was to compare the fracture toughness of 3 mol % Y2O3-stabilized ZrO2 sintered in a conventional or micro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1990
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.39.1556