Fracture on cylindrical FRP by internal pressure.

Semi Analytical Analysis of FGM Thick-Walled Cylindrical Pressure Vessel with Longitudinal Variation of Elastic Modulus under Internal Pressure

In this paper, a numerical analysis of stresses and displacements in FGM thick-walled cylindrical pressure vessel under internal pressure has been presented. The elastic modulus is assumed to be varying along the longitude of the pressure vessel with an exponential function continuously. The Poisson’s ratio is assumed to be constant. Whereas most of the previous studies about FGM thick-walled p...

Influence of initial geometric imperfections on the stability of thick cylindrical shells under internal pressure

Effect of Material Gradient on Stresses of FGM Rotating Thick-Walled Cylindrical Pressure Vessel with Longitudinal Variation of Properties under Non-uniform Internal and External Pressure

The present paper provides a semi-analytical solution to obtain the displacements and stresses in a functionally graded material (FGM) rotating thick cylindrical shell with clamped ends under non-uniform pressure. Material properties of cylinder are assumed to change along the axial direction according to a power law form. It is also assumed that the Poisson’s ratio is constant. Given the exist...

Fracture response of externally flawed aluminum cylindrical shells under internal gaseous detonation loading

Abstract. Experiments were performed to observe the fracture behavior of thinwall and initially-flawed aluminum tubes to internal gaseous detonation loading. The load can be characterized as a propagating pressure jump with speed of 2.4 km/s and magnitude ranging from 2 to 6 MPa, followed by an expansion wave. Flaws were machined as external axial surface notches. Cracks ran both in the upstrea...

Fracture Response of Externally Flawed Cylindrical Shells to Internal Gaseous Detonation Loading

Experiments were performed to observe the fracture behavior of thin-wall and initially-flawed aluminum tubes to internal gaseous detonation loading. The pressure load, with speeds exceeding 2 km/s, can be characterized as a pressure peak (ranging from 2 to 6 MPa in these experiments) followed by an expansion wave. Flaws were machined as external axial surface notches. Cracks ran both in the ups...