Fracture Characteristics and Microstructures of Intermetallic Compound Ti-24Al-11Nb(at%)
نویسندگان
چکیده
منابع مشابه
Time-temperature transformation behavior of Ti-24Al- 11Nb
The time-temperature transformation behavior of a rapidly solidified (RS) Ti-24Al-11Nb alloy has been studied between 450 and 850 “C using X-ray diffraction, electron diffraction, transmission electron microscopy and microindentation methods. A revised isothermal transformation path from the initial B2 to the final cz? structure has been proposed: B2 (Pmjm)B19 (Pmma)-0’ (Cmcm) 0’ (Cmcm) a2 (P6,...
متن کاملANALYTICAL DATA FOR NiO REDUCTION AND Al3Ni2 INTERMETALLIC COMPOUND FORMATION
In this research, the nickel oxide was dissolved in cryolite at temperatures of 880, 940 and 1000°C. In order to reduce the nickel oxide, aluminum was added to the salt. Simultaneously the nickel oxide was reduced and Al3Ni2 intermetallic compound was formed. In the duration intervals of 2.5-40 minutes samples of the salt and metallic phases were taken. The variation of the nickel content in me...
متن کاملComparison of the Microstructure, Tensile, and Creep Behavior for Ti-24Al-17Nb-0.66Mo (Atomic Percent) and Ti-24Al-17Nb-2.3Mo (Atomic Percent) Alloys
The effect of small molybdenum additions, 0.66 and 2.3 at. pct, on the microstructure, tensile, and creep behavior of a nominally Ti-24Al-17Nb (at. pct) alloy was investigated. The alloy containing 2.3 at. pct Mo contained higher body-centered-cubic (bcc) phase volume fractions, which was expected as Mo stabilizes the bcc phase. Constant load, tensile-creep experiments were performed in the str...
متن کاملMagnetic behaviour of the intermetallic compound YbCo2Si2
We report on a comprehensive study of the magnetic properties of YbCo2Si2 investigated using a single crystal. All data confirm a stable trivalent Yb state carrying a well-localized 4f moment, as well as a non-magnetic Co state. We observed a sizeable anisotropy in the magnetic susceptibility χ(T ), with the moment in the basal plane twice as large as that along the c-direction. Combining this ...
متن کاملMechanical milling of the intermetallic compound AlFe
The intermetallic compound AlFe in its ordered B2 phase has been ground under Ar in a ball-milling device. The system evolution under mechanical work has been examined as a function of time of milling by x-ray diffraction, transmission Mössbauer spectroscopy, and differential scanning calorimetry. Short and long range disorder was observed. The evolution of the long range order parameter with m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1995
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.59.7_708