Fracture Behavior of Multi-phase Fe-Zn Intermetallic Compound Layer
نویسندگان
چکیده
منابع مشابه
Electron Diffraction Study on Fe–Zn intermetallic Phase of a Galvannealed IF Steel Sheet
In order to investigate the structure of Fe–Zn phase in a commercial galvannealed IF steel sheet, the electron diffraction and composition of phase in a commercial galvannealed IF steel sheet were studied by transmission electron microscope (TEM) and X-ray energy dispersive spectroscopy (EDX). The cross-sectional TEM specimen was prepared using focused ion beam (FIB) technique which was also in...
متن کاملMagnetic phase transitions in intermetallic CeCuGe compound
Electrical and magnetic properties of CeCuGe were investigated through electrical resistivity, thermal conductivity and magnetization measurements in the temperature range 2–300 K. Magnetization measurements indicate a paramagnetic to ferromagnetic transition at TZ10 K, in agreement with previous work. There are two distinct paramagnetic regimes: At high-T the magnetic moment per cerium is 2.50...
متن کاملTribological Behaviour of Fe-Al Intermetallic Compound Coated Carbon Tool Steel
The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. The microstructure...
متن کاملTribological Behaviour of Fe-Al Intermetallic Compound Coated Carbon Tool Steel
The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour.
The microstructu...
متن کاملInvestigating the Joining of Ni3Al Intermetallic Compound, using Transient Liquid Phase (TLP) Method with Cu Interlayer
In this study, joining of Ni3Al intermetallic compounds using the transient liquid phase (TLP) process with Cu interlayer was investigated. The binding process was carried out in a vacuum furnace at a temperature of 1050 °C for different times of 30, 60, 90 and 120 minutes. The effect of time variation on microstructure and mechanical properties of the joint zone was investigated. The EDS analy...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 2016
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane.tetsu-2016-029