Fracture behavior in CFRP cross-ply laminates with initially cut fibers
نویسندگان
چکیده
منابع مشابه
Failure Criterion for Two-Ply Plain-Weave CFRP Laminates
We present an experimentally-based failure criterion for symmetric two-ply plain-weave laminates of carbon-fiber reinforced plastic. The criterion is formulated in terms of six force and moment stress resultants and consists of a set of three inequalities, related to in-plane, bending, and combined in-plane and bending types of failure. All failure parameters in the criterion are measured direc...
متن کاملPost-cure shape errors of ultra-thin symmetric CFRP laminates: Effect of ply-level imperfections
This paper discusses the effect of misalignments in ply orientation, uniform variations in ply thickness, and through-thickness thermal gradients on the post-cure shape errors for symmetric cross-ply laminates constructed from ultra-thin composite materials. Photogrammetry-based surface measurements are performed for laminates cured at elevated temperatures. Significant out-of-plane shape error...
متن کاملCompression Fracture of CFRP Laminates Containing Stress Intensifications
For brittle fracture behaviour of carbon fibre reinforced plastics (CFRP) under compression, several approaches exist, which describe different mechanisms during failure, especially at stress intensifications. The failure process is not only initiated by the buckling fibres, but a shear driven fibre compressive failure beneficiaries or initiates the formation of fibres into a kink-band. Startin...
متن کاملThe Formation and Effect of Outer-Ply Microcracks in Cross-Ply Laminates: A Variational Approach
The microcracking process in laminates which have outer-ply 90◦ plies (e.g. [90m/0n]s) has some important differences from the microcracking process in laminates which lack outer-ply 90◦ plies (e.g. [0n/90m]s). Foremost among the differences is the characteristic damage state. [90m/0n]s laminates form antisymmetric or staggered microcracks while [0n/90m]s laminates form symmetric microcracks. T...
متن کاملAcoustic emission monitoring of degradation of cross ply laminates.
The scope of this study is to relate the acoustic activity of damage in composites to the failure mechanisms associated with these materials. Cross ply fiber reinforced composites were subjected to tensile loading with recording of their acoustic activity. Acoustic emission (AE) parameters were employed to monitor the transition of the damage mechanism from transverse cracking (mode I) to delam...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Composites Part A: Applied Science and Manufacturing
سال: 2009
ISSN: 1359-835X
DOI: 10.1016/j.compositesa.2009.04.023