Fractographic Analysis of Strontium-Modified Al-Si Alloys

Study of the Mechanism and Causes of Pore Formation in Sr-modified Al-Si Alloys

The formation of microporosity in modified Al-Si alloys has been reviewed in the present study. A major concern in modification is the increased tendency to form microporosity in the macro-shrinkage free Al-Si alloy castings. It has also been demonstrated that at low hydrogen contents (0.1cc/ 100g, Al), where only shrinkage porosity should occur, the effect of Sr-modification on porosity conten...

Study of the Mechanism and Causes of Pore Formation in Sr-modified Al-Si Alloys

The formation of microporosity in modified Al-Si alloys has been reviewed in the present study. A major concern in modification is the increased tendency to form microporosity in the macro-shrinkage free Al-Si alloy castings. It has also been demonstrated that at low hydrogen contents (0.1cc/ 100g, Al), where only shrinkage porosity should occur, the effect of Sr-modification on porosity conten...

Precipitation Hardening of Al–Si–Mg Alloys

Revealing heterogeneous nucleation of primary Si and eutectic Si by AlP in hypereutectic Al-Si alloys.

The heterogeneous nucleation of primary Si and eutectic Si can be attributed to the presence of AlP. Although P, in the form of AlP particles, is usually observed in the centre of primary Si, there is still a lack of detailed investigations on the distribution of P within primary Si and eutectic Si in hypereutectic Al-Si alloys at the atomic scale. Here, we report an atomic-scale experimental i...

Creep Behavior of Al-Si Die-Cast Alloys

Commercial, aluminum die-cast alloys are subject to long-term stresses leading to viscoelastic material responses resulting in inefficient engine operation and failure. Constant load creep tests were conducted on aluminum die-casting alloys: B-390, eutectic Al-Si and a 17% Si-Al alloys. Rupture occurred in the primary creep regime, with the eutectic alloy having the longest times to failure. Pr...