Formation of periodic layered structure during hot-dip galvanizing in Al-Zn-Mg bath

REACTION KINETICS OF THE FORMATION OF INTERMETALLIC Fe – Zn DURING HOT - DIP GALVANIZING OF STEEL

P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic This review article mainly describes the composition of intermetallic Fe Zn, i.e. zeta (ζ), delta (δ1k + δ1p), gamma1 (Γ1) and gamma (Γ) on galvanized steel during low temperature galvanization (t ~ 450 °C). It gives detail...

Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating

The microstructure of continuously hot-dip galvanizing Zn-Mg coating was investigated in order to obtain the mechanism of the effects of Mg on the corrosion resistance. In this paper, the vertical section of the Zn-0.20 wt % Al-Mg ternary phase diagram near the Al-low corner was calculated. The results indicates that the phase composition of the Zn-0.20 wt % Al-Mg ternary phase diagram near the...

Exploring Carbide-Free Bainitic Structures for Hot Dip Galvanizing Products

Synthesis ratios of Mg-Al and Zn-Al layered double hydroxides efficiency and selectivity in nitrate removal from solution

Four diverse chlorides layered double hydroxides with diverse ratios, i.e. Mg-Al (3:1), Mg-Al (4:1), Zn-Al (4:1), and Zn-Al (3:1) LDHs, were prepared to evaluate their efficiency and selectivity towards nitrate removal from aquatic solutions. A batch experiment was done at the initial nitrate concentration of 5-1000 mg/L, pH 5 to 12, and contact time of 5-180 min. Isotherms of nitrate adsorptio...

Microstructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation

The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s-1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening m...