Formation of Medium Carbon TRIP Steel Microstructure During Annealing in the Intercritical Temperature Range
نویسندگان
چکیده
منابع مشابه
Austenite formation during intercritical annealing
Purpose: of this paper is the effect of the soft annealing of initial microstructure of the 6Mn16 steel on the kinetics of the austenite formation during next intercritical annealing. Design/methodology/approach: Analytical TEM point analysis with EDAX system attached to Philips CM20 was used to evaluate the concentration of Mn, Ni and Cr in the microstructure constituents of the multiphase ste...
متن کاملEffect of NbMo Addition on the Precipitation Behaviour of V Microalloyed Steel during Intercritical Annealing
This paper reports on the precipitation behaviour and microstructural evolution in ~20% cold rolled NbMoV and V single microalloyed low carbon steels during intercritical annealing. The microstructure and precipitation behaviour were studied by optical and scanning/transmission electron microscopy and microanalysis, X-ray diffraction technique and Vickers hardness testing. After intercritical a...
متن کاملEffects of Intercritical Annealing Temperature on Mechanical Properties of Fe-7.9Mn-0.14Si-0.05Al-0.07C Steel
A medium Mn steel has been designed to achieve an excellent combination of strength and ductility based on the TRIP (Transformation Induced Plasticity) concept for automotive applications. Following six passes of hot rolling at 850 °C, the Fe-7.9Mn-0.14Si-0.05Al-0.07C (wt.%) steel was warm-rolled at 630 °C for seven passes and subsequently air cooled to room temperature. The sample was subseque...
متن کاملIdentification of Retained Austenite, Ferrite, Bainite and Martensite in the Microstructure of TRIP Steel
Transformation induced plasticity (TRIP) steels have a vast application in automotive industry because of theirhigh strength, high ductility and hence excellent energy absorption capacity. These characteristics of TRIPsteels are due to the existence of retained austenite in their microstructures in the ambient temperature, whichtransforms to the martensite phase during deforma...
متن کاملControlling the Mechanical Properties and Corrosion Resistance of Mild Steel by Intercritical Annealing and Subcritical Tempering
The effects of intercritical annealing and subcritical tempering on the mechanical properties and corrosion resistance of mild steel were studied. It was revealed that intercritical annealing followed by quenching resulted in the development of a ferritic-martensitic dual phase (DP) microstructure with high tensile strength, disappearance of the yield-point phenomenon, superior work-hardening b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Archives of Metallurgy and Materials
سال: 2014
ISSN: 2300-1909
DOI: 10.2478/amm-2014-0170