X-ray Stress Measurement for Ni-Al System Intermetallic Compound Prepared by SHS- method
An X-ray diffraction technique was used to measure the residual stress in the surface of a specimen containing a coating of a NijAl intermetallic compound produced bythe SHS (Self-propagation High temperature Synthesis) method. The Ni3Al was using the coating material for spherical carbon cast iron substrate and austenite stainless steel substrate. Differences between the coefftcient of thermal...
متن کاملANALYTICAL DATA FOR NiO REDUCTION AND Al3Ni2 INTERMETALLIC COMPOUND FORMATION
In this research, the nickel oxide was dissolved in cryolite at temperatures of 880, 940 and 1000°C. In order to reduce the nickel oxide, aluminum was added to the salt. Simultaneously the nickel oxide was reduced and Al3Ni2 intermetallic compound was formed. In the duration intervals of 2.5-40 minutes samples of the salt and metallic phases were taken. The variation of the nickel content in me...
متن کاملControl of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel
The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...
متن کاملAn Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملIntermetallic phase formation during arnnealing of AI/Ni muMayers
The phase evolution during annealing of AlJNi multilayer samples prepared by ion-beam sputtering with composition modulation wavelengths A between 10 and 400 nm was determined using x-ray diffraction and differential scanning calorimeter measurements. Samples with average compositions of &n,N10,6,, and Al,,,N&,~ were investigated. For the Al,,40Ni0.60 samples the following results were obtained...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 2016
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet.j2016005