Formation Mechanism of Slab Surface Transverse Cracking in Continuously Cast Ni Bearing Steel
نویسندگان
چکیده
منابع مشابه
Assessment of Surface Defects in the Continuously Cast Steel
The development of continuous casting to produce semi-finished products is now so far advanced that almost any grade of steel can be continuously cast, and in the most appropriate cross section for further shaping. High quality finished products can only be produced by using defect free slabs, blooms or billet. The removal of defects is either performed selectively by removing the specific defe...
متن کاملsuppression of coke formation in thermal cracking by coke inhibitors
the main purpose of this research was to:1.develop a coking model for thermal cracking of naphtha.2.study coke inhibition methods using different coke inhibitors.developing a coking model in naphtha cracking reactors requires a suitable model of the thermal cracking reactor based on a reliable kinetic model.to obtain reliable results all these models shall be solved simultaneously.for this pu...
15 صفحه اولAutomatic Detection and Localization of Surface Cracks in Continuously Cast Hot Steel Slabs Using Digital Image Analysis Techniques
Quality inspection is an indispensable part of modern industrial manufacturing. Steel as a major industry requires constant surveillance and supervision through its various stages of production. Continuous casting is a critical step in the steel manufacturing process in which molten steel is solidified into a semi-finished product called slab. Once the slab is released from the casting unit, th...
متن کاملThe Effects of Hot Tear Segregations on the Rolled Product Quality of Continuously Cast Steel
The main objective of this project was to investigate the behavior and the damaging effects of hot tear segregations in the continuously cast steel blooms on the final product quality. To achieve this aim, plant data from three different types of steels were used. Investigations using the scanning electron microscope (SEM) equipped with energy dispersive x-ray spectroscopy (EDS) probe and metal...
متن کاملNumerical Simulation and Process Optimization on Cast Steel Bearing Sleeve
Article history: Received:29.09.2013. Received in revised form: 17.12.2013. Accepted: 24.12.2013. A three-dimensional Computer Aided Design (CAD) model of the bearing sleeve casting is established by Pro/E software. The ViewCast program is utilized for studying casting processes of solidification and mould-filling in order to optimize the casting technology. Based on the solidification simulati...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1998
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.84.12_856