Formation kinetics and cation inversion in mechanically activated MgAl2O4 spinel ceramics
نویسندگان
چکیده
منابع مشابه
Stable cation inversion at the MgAl2O4(100) surface.
From an interplay of atom-resolved noncontact atomic force microscopy, surface x-ray diffraction experiments, and density functional theory calculations, we reveal the detailed atomic-scale structure of the (100) surface of an insulating ternary metal oxide, MgAl2O4 (spinel). We surprisingly find that the MgAl2O4(100) surface is terminated by an Al and O-rich structure with a thermodynamically ...
متن کاملFaulted defect aggregates in neutron-irradiated MgAl2O4 spinel
Single crystals of stoichiometric MgA1204 spine1 were neutron-irradiated to fluences (> 0.1 MeV) of 2.8 x loz5 n m-2 (1.5 dpa) at 1015 K and 1.9 x loz6 n m-2 (10 dpa) at 925 K and 1 100 K. The resulting point defect'aggregates were investigated using bright-field and weak-beam dark-field transmission electron microscopy. For the higher dose, faulted interstitial Frank dislocation loops were fou...
متن کاملIn-situ neutron diffraction study of non-convergent cation ordering in the (Fe3O4)1-x(MgAl2O4)x spinel solid solution
Non-convergent cation ordering in the (Fe3O4)1-x(MgAl2O4)x solid solution was investigated using in-situ time-of-flight neutron powder diffraction. The approach to equilibrium in a sample with x = 0.75 was observed at 923 K by performing in-situ structure refinements at intervals of 5 min, and the ordering behavior was traced through the time-dependence of the lattice parameter, the cation-oxyg...
متن کاملUnique mechanical properties of nanostructured transparent MgAl2O4 ceramics
Nanoindentation tests were performed on nanostructured transparent magnesium aluminate (MgAl2O4) ceramics to determine their mechanical properties. These tests were carried out on samples at different applied loads ranging from 300 to 9,000 μN. The elastic recovery for nanostructured transparent MgAl2O4 ceramics at different applied loads was derived from the force-depth data. The results revea...
متن کاملMagnetic Cation Distribution in Nanocrystalline Fe3O4 Spinel
Neutron diffraction study of nanostructured magnetite was performed at room temperature. The actual grain-size was determined from evaluation of X-ray diffraction profiles by the modified Williamson-Hall plot. The atomic structure parameters and the sublattice magnetic moments were determined using the Rietveld refinement of the neutron diffraction spectra. The sublattice magnetization at the o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Thermal Analysis and Calorimetry
سال: 2019
ISSN: 1388-6150,1588-2926
DOI: 10.1007/s10973-019-08846-w