Foreward for special issue on "Al-Li alloys"
نویسندگان
چکیده
منابع مشابه
Zener Relaxation in Al-Li Binary Alloys
Internal friction (I.F.) and modulus measurements have been carried out as a function of temperature in order to study the Li mobility in an A1 8.1 at% Li 0.03 at% Zr alloy. The results show that the sequence of 6' and 6 precipitation can be followed through the evolution of the internal friction spectra. Two peaks appear in the internal friction spectrum. The low temperature peak Pz (450 K), h...
متن کاملDECOMPOSITION IN BINARY Al-Li ALLOYS
We have investigated the influence of aging on the morphology and phase composition of annealed Al-Li binary alloys by means of an atom probe with a multi-detection system. The influence of artifacts such as the preferential evaporation of the Li-atoms and the pile-up effects for the Al-atoms were analysed as well. Specimens of Al 2.0 wt%Li andAl -2.9 wt%Li were solution treated and aged at 190...
متن کاملCASTABILITY OF Al-Li-Mg AND Al-Li-Cu-Mg ALLOYS
The objective of the present work is to study the casting characteristics of various A1-Li alloys, which include fluidity and strengths of the alloys and their interaction with cast molds. Materials investigated are Al-Li-Mg and Al-Li-Cu-Mg alloys with Li content of 2.5 wt%. The results show that sand molds with resin binders are good for A1-Li casting. Ceramic coatings can further reduce the m...
متن کاملEffects of Li additions on precipitation-strengthened Al–Sc and Al–Sc–Yb alloys
Two Al–Sc-based alloys (Al–0.12Sc and Al–0.042Sc–0.009Yb, at.%) and their counterparts with Li additions (Al–2.9Li–0.11Sc and Al–5.53Li–0.048Sc–0.009Yb, at.%) are aged at 325 C. For both base alloys, the addition of Li results in greater peak hardness from incorporation of Li in the L12-structured a-Al3(Sc,Li) and a-Al3(Sc,Li,Yb) precipitates, and a concomitant increase in number density and vo...
متن کاملAN ATOM-PROBE ANALYSIS OF Al-Li ALLOYS
The aging process in A1-Li alloys was studied by an atom-probe FIM. Two types of precipitates were recognized in the FIM image, one is brightly imaged with a high degree of order in its structure and the other appeared dark against the Al matrix. Atom-probe analysis showed that the Li concentration is in a range of 10 to 25 at% in the dark precipitate and approximately 25 at% in the bright prec...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1986
ISSN: 0451-5994
DOI: 10.2464/jilm.36.683