Fluxless Tin Bonding Process With Suppressed Intermetallic Growth
نویسندگان
چکیده
منابع مشابه
Fluxless Process of Fabricating In–Au Joints on Copper Substrates
Based on the oxidation-free fluxless bonding technology, we have developed a bonding process to manufacture In–Au joints on copper substrates. 4 mm 4 mm Si blank dice and 6 mm 6 mm copper substrates are used. The dice are deposited with indium-rich Au/In/Cr multilayer structure in a single high vacuum cycle to prevent oxidation. Right after deposition, the outer Au layer interacts with the In l...
متن کاملIntermetallic Compounds of Element 112: the Electronic Structure and Bonding
The next heaviest element which is to be studied chemically at the JINR, Dubna, [1] and GSI [2] is element 112. Its properties are expected to be unique: high volatility and inertness due to the very strong relativistic stabilization of the 7s electrons and the closed-shell configuration, 7s6d [3]. The surface of the chromatography column in the gas-phase chromatography experiments is to be mad...
متن کاملCopper/solder intermetallic growth studies.
Copper samples, hot solder (eutectic) dipped and thermally aged, were cross-sectioned and placed in an environmental scanning electronic microscope (ESEM). While in the ESEM the samples were heated for approximately 2.5 h at 170 degrees C to stimulate the growth of additional Cu/Sn intermetallic compound. The intent of the study was to obtain a continuous real-time videotape record of the diffu...
متن کاملFluxless silicon-to-alumina bonding using electroplated Au–Sn–Au structure at eutectic composition
Large 6 mm× 9 mm silicon chips have been successfully bonded to alumina substrates with electroplated Au/Sn/Au structure at the eutectic omposition. The new bonding process is entirely fluxless, or flux-free. It is performed in vacuum (50 milliTorrs), where the oxygen content is educed by a factor of 15,200 comparing to air, to inhibit solder oxidation. Eutectic Au80Sn20 alloy is a well establi...
متن کاملStannylplumbylenes: bonding between tetravalent tin and divalent lead.
Depending on stoichiometry, reactions of the mixed valence Sn(0)/Sn(III) compound Sn(SnAr(3))(2) (1) (Ar = C(6)H(4)(O(i)Pr)(2)-2,6) with the likewise substituted plumbylene PbAr(2) (3) afforded either the homoleptic distannylplumbylene Pb(SnAr(3))(2) (4) or the heteroleptic arylstannylplumbylene Pb(Ar)SnAr(3) (5), a valence isomer of a stannaplumbene.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IEEE Transactions on Components, Packaging and Manufacturing Technology
سال: 2014
ISSN: 2156-3950,2156-3985
DOI: 10.1109/tcpmt.2014.2300476