Flow Behavior of High Molecular Weight Polyethylene

Synthesis of high molecular weight polyethylene using FI catalyst

A FI Zr-based catalyst of bis[N-(3,5-dicumylsalicylidene)-2′,6′­diisopropylanilinato]zirconium(IV) dichloride was prepared and used for polymerization of ethylene. The effects of reaction conditions on the polymerization were examined in detail. The increase in ethylene pressure and rise in polymerization temperature up to 35 oC were favorable for catalyst/MAO to raise the catalytic activity as...

Wear of Ultra High Molecular Weight Polyethylene

synthesis of high molecular weight polyethylene using fi catalyst

a fi zr-based catalyst of bis[n-(3,5-dicumylsalicylidene)-2′,6′­diisopropylanilinato]zirconium(iv) dichloride was prepared and used for polymerization of ethylene. the effects of reaction conditions on the polymerization were examined in detail. the increase in ethylene pressure and rise in polymerization temperature up to 35 oc were favorable for catalyst/mao to raise the catalytic activity as...

Friction and wear behavior of ultra-high molecular weight polyethylene as a function of polymer crystallinity.

In this study the friction, wear and surface mechanical behavior of medical-grade ultra-high molecular weight polyethylene (UHMWPE) (GUR 1050 resin) were evaluated as a function of polymer crystallinity. Crystallinity was controlled by heating UHMWPE to a temperature above its melting point and varying the hold time and cooling rates. The degree of crystallinity of the samples was evaluated usi...

Effect of cyclic strain on the mechanical behavior of virgin ultra-high molecular weight polyethylene.

Ultra High Molecular Weight Polyethylene (UHMWPE) is a polymeric material employed in critical biomedical applications. Knowledge of its mechanical behavior is essential in order to obtain accurate prediction of stresses and deformations in real components, in particular when cyclic loading is considered. In the present research the effects of alternating and pulsating cyclic strain on the mech...