Fireside corrosion on T24 steel pipes and HVOF NiCr coatings exposed to different salt mixtures
نویسندگان
چکیده
منابع مشابه
High Temperature Corrosion Behavior of HVOF, Fe3Al Coatings
This work evaluates the suitability of iron aluminide coatings for use in high temperature fossil fuel combustion environments, such as boiler applications. The coatings are applied using High Velocity Oxy-Fuel (HVOF) thermal spray techniques. Bulk Fe3Al coatings are known to exhibit excellent oxidation and sulfidation resistance at high temperatures, however, the behavior of HVOF-deposited Fe3...
متن کاملHydrophobic and superhydrophobic coatings for corrosion protection of steel
Since metals in general, and steels in particular, are vital construction materials in our modern society, the corrosion protection of said materials is of great importance, both to ensure safety and to reduce costs associated to corrosion. Previously, chromium (VI) and other harmful substances were effectively used to provide corrosion protection to steel, but since their use was heavily regul...
متن کاملHot corrosion behavior of HVOF-sprayed CoNiCrAlYSi coatings in a sulphate environment
HVOF-sprayed CoNiCrAlYSi coatings were tested at 900 °C in a hot corrosion environment containing sodium-potassium sulphates. The HVOF spraying caused the typical splat-on-splat structure. The results after the hot corrosion testing showed that the corrosion preferentially occurred at the coating surface and the splat boundaries. The oxidation along the splat boundaries can isolate the splat fr...
متن کاملCorrosion Tests of Steel Earthing Electrodes with Protective Coatings Made from Different Materials
In the paper the methodology and test results of field and laboratory corrosion tests of steel earthing rods with zinc galvanized coatings and copperbonded coatings are described. The corrosion rate and level of corrosion damage of earthing rods with two different protective coatings have been compared as well some conclusions related to reliability and assessment of technical life time of st...
متن کاملCorrosion Protection of Steel Using Nonanomalous Ni-Zn-P Coatings
A novel technique for obtaining nonanomalous Ni-Zn-P coatings with high Ni content ~74 wt % as compared to 15-20 wt % in the conventional plating method! has been developed. These coatings show promise as a replacement for Cd in sacrificially protecting steel. Ni-Zn-P coatings were deposited using an electroless method from a solution containing NiSO4 , complexing agent and ammonium chloride. V...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Science
سال: 2020
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2020.108747