Field Emission Characteristics ofSnO2/CNTs Composites Prepared by Microwave-Assisted Wet Impregnation
نویسندگان
چکیده
منابع مشابه
Methane oxy-steam reforming over a highly efficient Ni/Al2O3 nanocatalyst prepared by microwave-assisted impregnation method
An alumina-supported nickel catalyst was prepared by impregnation of Ni2+ solution onto mesoporous alumina under microwave irradiation (denoted as M-Ni/Al2O3). For comparison, a catalyst with the same nickel content was prepared by conventional impregnation method (denoted as UM-Ni/Al2O3). Both M-Ni/Al2O3 and UM-Ni/Al2O3 catalysts were applied to the syngas (H2 + CO) production by methane oxy-s...
متن کاملMicrowave Absorption and Infrared Stealth Characteristics of Bamboo Charcoal/Silver Composites Prepared by Chemical Reduction Method
Bamboo charcoal coated with silver (BC/Ag) was prepared by activation and chemical reduction processes at different AgNO3 contents (10-30 wt.%). The spectroscopic characterizations of the formation processes of BC/Ag composites were studied using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. These composites were introduced in epoxy resin to be a microwav...
متن کاملExcellent Field Emission Properties of Short Conical Carbon Nanotubes Prepared by Microwave Plasma Enhanced CVD Process
Randomly oriented short and low density conical carbon nanotubes (CNTs) were prepared on Si substrates by tubular microwave plasma enhanced chemical vapor deposition process at relatively low temperature (350–550 C) by judiciously controlling the microwave power and growth time in C2H2 + NH3 gas composition and Fe catalyst. Both length as well as density of the CNTs increased with increasing mi...
متن کاملCharacteristics of Acoustic Emission Signals from Composites
Certain characteristics of acoustic emission (AE) signals from graphite-epoxy composite specimens were correlated last year with the mechanical behavior of the materials. Moisture degradation, which reduced the ultimate strength, resulted in a change in the AE amplitude distribution early in the loading history. Also, AE having distinct frequency spectral types tended to occur at or near singul...
متن کاملMicrowave-Assisted Sintering of Al–ZrO2 Nano-Composites
Abstract In this project, nano-ZrO2 particles were dispersed in aluminum powder by a Y-shape mixer. The particle size of ZrO2 powder was < 40 nm and the amount of ZrO2 reinforcement varies from 3 to 15%.The mixed powders were compacted .Subsequently the compacted discs were sintered both in the microwave oven and in the conventional muffle furnace .Using microwave –assisted sintering method led...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Nanomaterials
سال: 2012
ISSN: 1687-4110,1687-4129
DOI: 10.1155/2012/861591