Ferromagnetic-like behaviour in bismuth ferrite films prepared by electrodeposition and subsequent heat treatment
نویسندگان
چکیده
منابع مشابه
AgInSe2 thin films prepared by electrodeposition process
In this work, the one step electrodeposition process was used to prepare Ag-In-Se thin films. The films were deposited at room temperature from a bath containing 1-3x10 M AgNO3, 6x10 -2 M InCl3 and 3x10 -2 M of H2SeO3. The KSCN at a concentration of 0.681 M was used as complexing agent. The pH value of the solution was 1.4. Applied potentials to SCE were chosen between -0.3 V and -1.1 V. Films ...
متن کاملTEM Characterization and Properties of Cu-1 wt.% TiB2 Nanocomposite Prepared by Rapid Solidification and Subsequent Heat Treatment
Copper matrix composite reinforced by 1wt.% TiB2 particles was prepared using in situ reaction of Cu-1.4wt.% Ti and Cu-0.7wt.% B by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºC. High-resolution transmission electron microscopy (HRTEM) characterization showed that primary TiB2 particles were formed in liquid copper. Heat treatment of as-solidified samples led to ...
متن کاملPhysical properties of CdSexTe1-x thin films prepared by electrodeposition
The cadmium chalcogenides CdSexTe1-x ( 1 x 0 ≤ ≤ ) thin films have been electrodeposited onto ITO coated glass substrates from an acid sulfate solution at 90 °C. The structure, the composition and the morphology have been studied as a function of the x coefficient by XRD, EDAX, optical absorbance and AFM techniques. All deposits have a cubic structure with a preferred orientation along the (111...
متن کاملPreparation of Gd2O3 Ultrafine Nanoparticles by Pulse Electrodeposition Followed by Heat-treatment Method
Gd2O3 nanoparticles were prepared by a two–step process; cathodic electrodeposition followed by heat-treatment method. First, Gd(OH)3 nanoparticles was galvanostatically deposited from nitrate bath on the steel substrate by pulse current (PC) mode. The deposition experiments was conducted at a typical on-time and off-time (ton=1ms and toff=1ms) for 60 min. The electrodeposited precursor was the...
متن کاملtem characterization and properties of cu-1 wt.% tib2 nanocomposite prepared by rapid solidification and subsequent heat treatment
copper matrix composite reinforced by 1wt.% tib2 particles was prepared using in situ reaction of cu-1.4wt.% ti and cu-0.7wt.% b by rapid solidification and subsequent heat treatment for 1-20 hrs at 900ºc. high-resolution transmission electron microscopy (hrtem) characterization showed that primary tib2 particles were formed in liquid copper. heat treatment of as-solidified samples led to the f...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2017
ISSN: 2046-2069
DOI: 10.1039/c7ra04375a