Fatigue Test of Coated Mild Steel with Nickel and Aluminum
نویسندگان
چکیده
منابع مشابه
Investigations on Tensile Strength of Aluminium and Nickel Coated Aluminum
Electro less deposition is an autocatalytic chemical technique to deposit a coating of metal on a work piece with the presence of a reducing agent. Electro less nickel coating has high advantages in electroplating. In this work the changing structure of nickel deposits on aluminum and its alloys at the early stage of electro less nickel deposition using sodium hypophosphite ion used as reducing...
متن کاملOxidation resistance of plasma coated and laser treated mild steel
Stainless steel powder was coated on mild steel substrate using plasma coating. The porous coating thus obtained was modified using laser irradiation. The oxidation behaviour of the plasma coated as well as laser treated material was studied in air at 1073 K. There was considerable decrease in oxidation rate of mild steel after plasma coating as expected. In addition the oxidation resistance im...
متن کاملEffect of nitriding temperature on the nanostructure and corrosion properties of Nickel coated 304 stainless steel
Nickel films of 150 nm thickness were deposited on 304 stainless steel and post annealed under flow of nitrogen at different temperatures. The prepared samples were corrosion tested in 1.0 M H2SO4 solution using potentiodynamic polarization technique. Crystallographic and morphological structure of the samples were analysed by X-ray diffraction XRD and atomic force microscopy AFM respectively b...
متن کاملCyclic oxidation behavior of uncoated and aluminum-rich nickel aluminide coated Rene-80 superalloy
In this study, aluminide coating was employed to enhance the high-temperature cyclic oxidation of Rene-80 superalloy at 950ºC. The microstructural aspects and phase constituents of samples were investigated with scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques. The result of oxidation tests showed that the weight gain in the uncoated sample was considerably higher than...
متن کاملStrength and Toughness of Reinforced Concrete with Coated Steel Fibers
The effect of zinc phosphate (ZP) and zinc calcium phosphate (ZCP) coatings on the reinforcing mechanisms of smooth steel fiber in cementitious matrix have been studied. The results of pull out tests illustrated that by coating smooth steel fiber the pull-out load may be increased up to 100%. The effect of zinc phosphate coating on interface bonding was more than zinc-calcium phosphate coating....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Rafidain Journal of Science
سال: 2013
ISSN: 2664-2786
DOI: 10.33899/rjs.2013.67486