Fatigue Strength of Gusset Welded Joints under Simulated Program Loading of Overhead Travelling Crane.
نویسندگان
چکیده
منابع مشابه
Fatigue Behaviour of CFRP Strengthened Out-of-Plane Gusset Welded Joints with Double Cracks
This paper investigates the fatigue behaviour of out-of-plane gusset welded joints strengthened with carbon fibre reinforced polymer (CFRP) laminates. Two notches were introduced at the weld toes adjacent to longitudinal plate ends to simulate the initial damage. Variables including the stress range, singleor double-sided strengthening and modulus of CFRP materials were considered. It was found...
متن کاملImproving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملEffect of UIT on Fatigue Life in Web-Gusset Welded Joints
Ultrasonic impact treatment (UIT), which is a peening method, is usually used as a post-weld treatment in order to improve the fatigue strength of welded joints. In this study, fatigue tests were carried out on web-gusset welded joints treated by UIT and the results were compared with the fatigue lives of as-welded joints in order to examine the effects of UIT on the fatigue lives of welded joi...
متن کاملFatigue Behaviour of Al 6082-T6 Friction Stir Welded Tubular Joints under Torsional Loading
The aim of the present research is to investigate the fatigue behaviour of friction stir (FS) welded tubular joints in aluminium alloy subjected to torsional fatigue loading. To manufacture the samples which were tested, an MTS I-STIR process development system was equipped with a retracting tool specifically designed for these tubular welds. Al 6082-T6 FS welded samples were tested under cycli...
متن کاملUltra low cycle fatigue of welded steel joints under multiaxial loading
Ultra low cycle fatigue (ULCF) is a phenomenon that can be summarily defined as the deterioration of material properties under high amplitude cyclic loading, under which failure is reached typically within ten to twenty cycles. This phenomenon is observed in extreme loading scenarios such as earthquakes or exceptional winds where large cyclic strains are expected. Particularly sensitive are str...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: JSME International Journal Series A
سال: 1998
ISSN: 1344-7912,1347-5363
DOI: 10.1299/jsmea.41.112