Fatigue Strength Improvement by Replacing Welded Joints with Ductile Cast Iron Joints
نویسندگان
چکیده
منابع مشابه
Improving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملFatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملEnhancing fatigue strength by Ultrasonic Impact Treatment for welded joints of offshore structures
This paper summarises fatigue tests on Y-joints to estimate the influence of a post weld treatment method called Ultrasonic Impact Treatment. With this method the fatigue resistance could be increased significantly. Furthermore, tubular joints of tripod structures for offshore wind energy converters are analysed with numerical simulations to judge these welded joints with the hot-spot-concept. ...
متن کاملInvestigation of the Fatigue Strength of the Welded Joints Treated by Tig Dressing
The fatigue fracture of structural details subjected to cyclic loads mostly occurs at a critical cross section with stress concentration. The welded joint is particularly dangerous location because of sinergetic harmful effects of stress concentration, tensile residual stresses, deffects, microstructural heterogeneity. Because of these reasons many methods for improving the fatigue resistance o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 2019
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane.tetsu-2018-158