Fatigue Property Analysis of Rail Steel Based on Damage Mechanics
نویسندگان
چکیده
منابع مشابه
Progressive Damage Analysis of Laminated Composites using Continuum Damage Mechanics
In this paper, progressive damage and global failure of composite laminates under quasi-static, monotonic loading are investigated using 3D continuum damage mechanics. For this purpose, a finite element program has been developed using an eight-node 2D layered element including layer-wise plate theory. Damage analysis of a single orthotropic layer under various uniform in-plane and transverse l...
متن کاملFatigue Failure of Structural Steel – Analysis Using Fracture Mechanics
Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This pa...
متن کاملA Thermodynamics Based Damage Mechanics Framework for Fatigue Analysis of Microelectronics Solder Joints with Size Effects
Experimental observations of an increase in resistance with decreasing specimen size and under the presence of non-uniform plastic deformation fields have pushed the development for small scale plasticity theories since the early 90’s. The observed phenomenon has been explained in terms of an accumulation of a density of geometrically necessary dislocations, which is required in order to accomm...
متن کاملCHARACTERIZATION OF TRANSVERSE CRACK AND CRACK GROWTH IN A RAILWAY RAIL
Abstract: To ensure the rail transportations safety, evaluation of fatigue behavior of the rail steel is necessary. High cycle fatigue behaviour of a rail steel was the subject of investigation in this research using fracture mechanics. Finite element method (FEM) was used for analyzing the distribution of the stresses on the rail, exerted by the external load. FEM analysis showed that the ...
متن کاملExperimental Analysis of Fracture and Damage Mechanics of Pre-Stressed Concrete Sleepers B70: Part B- Analysis
Initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. These cracks may lead to complete failure of the structure. In order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. In order to achieve this purpose, it is important to fore...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Quarterly Report of RTRI
سال: 2004
ISSN: 0033-9008,1880-1765
DOI: 10.2219/rtriqr.45.203