FATIGUE OF STEEL REINFORCEMENT BARS IN CONCRETE: A REVIEW
نویسندگان
چکیده
منابع مشابه
Monitoring Corrosion of Steel Bars in Reinforced Concrete Structures
Corrosion of steel bars embedded in reinforced concrete (RC) structures reduces the service life and durability of structures causing early failure of structure, which costs significantly for inspection and maintenance of deteriorating structures. Hence, monitoring of reinforcement corrosion is of significant importance for preventing premature failure of structures. This paper attempts to pres...
متن کاملFatigue of Reinforcing Steel Bars Subjected to Natural Corrosion
Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...
متن کاملbond strength of reinforcement steel in self-compacting concrete
self-compacting concrete (scc) is a highly fluid yet stable concrete that can flow consistently under its own weight, pass between bars, and fill in formwork without the need of compaction. the application of scc effectively resolves the difficulties of concreting in situations with complicated formwork and congested reinforcements. in this paper, the bond between scc and steel reinforcement wa...
متن کاملStatic and Fatigue Behavior Investigation of Artificial Notched Steel Reinforcement
Pitting corrosion is one of the most common forms of localized corrosion. Corrosion pit results in a stress concentration and fatigue cracks usually initiate and propagate from these corrosion pits. Aging structures may fracture when the fatigue crack reaches a critical size. This paper experimentally simulates the effects of pitting morphologies on the static and fatigue behavior of steel bars...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Fatigue & Fracture of Engineering Materials and Structures
سال: 1979
ISSN: 8756-758X,1460-2695
DOI: 10.1111/j.1460-2695.1979.tb01084.x