Fatigue lifetime of AlBC 3 alloy by ultrasonic fatigue testing machine in cavitation regime
نویسندگان
چکیده
منابع مشابه
Fatigue and corrosion fatigue properties of Ti-6Al-4V implant grade titanium alloy in Ringer solution
Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-6Al-4V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning elect...
متن کاملFatigue and ultrasonic testing of epoxy-glass composites
Purpose: The purpose of this paper was to find relationship between the degree of strength degradation caused by fatigue and the changes of ultrasonic wave characteristics such as wave velocity and damping coefficient. Design/methodology/approach: Epoxy-glass composites were subjected to oscillatory bending loadings with constant deflection. During fatigue procedure the force needed to achieve ...
متن کاملEnhancing Fatigue Strength by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated in large-scale specimens having a nominal yield strength of 345 to 690 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating them by UIT. A par...
متن کاملFatigue Testing
Fatigue is the progressive, localized, permanent structural change that occurs in materials subjected to fluctuating stresses and strains that may result in cracks or fracture after a sufficient number of fluctuations. Fatigue fractures are caused by the simultaneous action of cyclic stress, tensile stress and plastic strain. If any one of these three is not present, fatigue cracking will not i...
متن کاملThe Effect of Various Parameters on Out-of-phase Thermo-mechanical Fatigue Lifetime of A356.0 Cast Aluminum Alloy
In this paper, the effect of various parameters on out-of-phase thermo-mechanical fatigue (OP-TMF) lifetime of A356.0 cast aluminum alloy is investigated. The studied parameters include maximum temperature, dwell time, and the thermo-mechanical loading factor. OP-TMF tests are conducted considering realistic running conditions of diesel engine cylinder heads. The maximum temperature varies betw...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Journal of Engineering
سال: 2015
ISSN: 2051-3305,2051-3305
DOI: 10.1049/joe.2015.0069