Fatigue Life Analysis of Crane K-Type Welded Joints Based on Non-Linear Cumulative Damage Theory
نویسندگان
چکیده
منابع مشابه
Fatigue Life Analysis of Crane K-Type Welded Joints Based on Non-Linear Cumulative Damage Theory
Engineering fatigue fracture failure is one of the most common phenomena of mechanical and structural failure, statistically representing approximately 50 to 90% of total mechanical damage [1]. Lattice structures have been widely used in crane booms, steel plants, parking garages, offshore platforms and other fields [2] to [4]. In a crane, the lattice boom has better mechanical properties compa...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملFatigue Life Prediction for Welded Joints with Known Initial Crack
The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...
متن کاملFatigue Life Assessment of Welded Joints Considering Crack Propagation Based on Hot Spot Stress
In this study, fatigue test and crack propagation analysis of welded joints in ships and offshore structures were performed. The test models have two types of welded joints, T-joint and double plate. Test data is presented in S-N curves obtained by the Hot Spot Stress (HSS) approach. The S-N data for each length of crack were appraised to define the fatigue life of crack initiation and propagat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Strojniški vestnik – Journal of Mechanical Engineering
سال: 2014
ISSN: 0039-2480
DOI: 10.5545/sv-jme.2013.1368