Fatigue failure analysis of HSLA steel sheets holed by conventional and flow drilling processes
نویسندگان
چکیده
منابع مشابه
Ductile Failure in High Strength Steel Sheets
Developments in computer-aided engineering and the rapid growth of computational power have made simulation-driven process and product development efficient and useful since it enables detailed evaluation of product designs and their manufacturing processes. In the context of a sheet metal component, it is vital to predict possible failure both during its forming process and its subsequent usag...
متن کاملEstimation of Maximum Inclusion Size and Fatigue Limit in HSLA-100 Steel
The objective of the current study is to determine the fatigue limit of a clean and high-performance material named as HSLA-100 steel and to compare the obtained fatigue limit with that of theoretically predicted fatigue limit by statistics of extreme value (SEV) method. Also, the size of inclusions located at the site of fatigue crack nucleation on the fracture surface of the fatigue test spec...
متن کاملFatigue Failure of Structural Steel – Analysis Using Fracture Mechanics
Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This pa...
متن کاملFailure of high strength steel sheets: Experiments and modelling
Failure in sheet metal structures of ductile material is usually caused by one of, or a combination of, ductile fracture, shear fracture or localised instability. In this paper the failure of the high strength steel Docol 600DP and the ultra high strength steel Docol 1200M is explored. The constitutive model used in this study includes plastic anisotropy and mixed isotropic-kinematic hardening....
متن کاملIdentification of Low Cycle Fatigue Parameters of High Strength Low-alloy (hsla) Steel at Room Temperature
S. Bulatović, Yugoslav River Shipping, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Matéria (Rio de Janeiro)
سال: 2019
ISSN: 1517-7076
DOI: 10.1590/s1517-707620190002.0689