Fatigue cracking of aluminium alloy AlZn6Mg0.8Zr subjected to thermomechanical treatment
نویسندگان
چکیده
منابع مشابه
X-ray analysis of polycrystalline aluminium subjected to fatigue cycling
Variations in the halfwidth values of X-ray reflections from fatigue-cycled, polycrystalline aluminium samples have been analysed. An oscillatory variation of the halfwidths with fatigue cycling has been observed. Analysis of the diffraction line profiles indicates that broadening arises mainly because of the build-up of microstrains during fatigue cycling. The present data indicate that (i) br...
متن کاملFatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy
This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...
متن کاملFatigue of Friction Stir Welded 2024-T351 Aluminium Alloy
Fatigue failure characteristics of friction stir welds in 13mm gauge 2024-T351 plate have been assessed. Failure occurred from either the weld region (nugget/flow arm) or from the material immediately surrounding the weld. Fatigue failure from the surrounding material was essentially conventional, initiating from large S-phase intermetallic particles and growing in a macroscopic mode I manner. ...
متن کاملDosimetry of Intense Particle Beams Using the Thermomechanical Behaviour of an Irradiated Aluminium Alloy
An hydrodynamic code coupled with a "PUFF-type" equation of state has been set up to investigate the thermomechanical behaviour of an aluminium alloy irradiated by a 1 MeV electron beam. The absorbed flux can reach 3500 J/cm2 with an exponential damping along 1 mm dep;th. A weaker flux .is produced with 1 MeV protons whose the stopping range is 10 pm for a 8000 J/g dose. Thermal stresses genera...
متن کاملThermomechanical Properties of TiNi Shape Memory Alloy
The thermomechanical properties of shape memory effect and superelasticity due to the martensitic transformation and the R-phase transformation of TiNi shape memory alloy were investigated experimentally. The transformation line, recovery stress and fatigue property due to both transformations were discussed for cyclic deformation. The thermomechanical properties due to the R-phase transformati...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frattura ed Integrità Strutturale
سال: 2015
ISSN: 1971-8993
DOI: 10.3221/igf-esis.35.51