Fatigue crack propagation behavior under stress changing in SCM 435 steel.
نویسندگان
چکیده
منابع مشابه
Influence of Residual Stress Field on the Fatigue Crack Propagation in Prestressing Steel Wires
This paper deals with the effect of several residual stress profiles on the fatigue crack propagation in prestressing steel wires subjected to tension loading or bending moment. To this end, a computer program was developed to evaluate the crack front evolution on the basis of the Walker law. Results demonstrate that the absence of residual stresses makes the crack propagate towards a preferent...
متن کاملFatigue of Yttria-Stabilized Zirconia: II, Crack Propagation, Fatigue Striations, and Short-Crack Behavior
Fatigue crack propagation in 3Y-TZP was investigated using controlled surface flaws. A unique growth law strongly dependent on the maximum stress intensity factor and quadratically dependent on the amplitude of the range of stress intensity factor was established. This growth law was found to apply for both surface flaws and internal flaws and could be used to predict fatigue lifetime. The pres...
متن کاملEffect of Mean Stress on Fatigue Crack Growth Behavior of Stainless Steel 304L
Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...
متن کاملFatigue-Crack Propagation Behavior of Ductile/Brittle Laminated Composites
A study has been made of the fatigue-crack propagation properties of a series of laminated Nbreinforced Nb3Al intermetallic-matrix composites with varying microstructural scale but nominally identical reinforcement volume fraction (20 pct Nb). It was found that resistance to fatigue-crack growth improved with increasing metallic layer thickness (in the range 50 to 250 mm) both in the crack-divi...
متن کاملCrack propagation and fracture in silicon wafers under thermal stress
The behaviour of microcracks in silicon during thermal annealing has been studied using in situ X-ray diffraction imaging. Initial cracks are produced with an indenter at the edge of a conventional Si wafer, which was heated under temperature gradients to produce thermal stress. At temperatures where Si is still in the brittle regime, the strain may accumulate if a microcrack is pinned. If a cr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1985
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.34.1187