Side Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملFatigue crack initiation in a notched single-crystal superalloy component
In this paper, the fatigue crack initiation in notched single-crystal test specimens of material MD2 is investigated and analysed. A critical plane approach is adopted, in which the total strain ranges on the discrete slip planes are evaluated. Furthermore, a Coffin-Manson type of expression is used to describe the number of cycles to fatigue crack initiation. This relation is determined from a...
متن کاملFatigue crack growth in a coarse-grained iron–silicon alloy
The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...
متن کاملA probabilistic method to predict fatigue crack initiation
A probabilistic method to predict macrocrack initiation due to fatigue damage is presented in this paper. Acoustic non-linearity is used to quantify pre-macrocrack initiation damage. This data is then used in a probabilistic analysis of fatigue damage. The probabilistic fatigue damage analysis consists of a suitably chosen damage evolution equation to model accumulated damage coupled with a pro...
متن کاملFatigue Crack Initiation and Multiplication of Unnotched Titanium Matrix Composites
ÐFatigue crack initiation and multiplication of the unnotched SCS-6 silicon carbide ®ber-reinforced titanium matrix composites with dierent matrix and interfacial properties have been investigated experimentally and analytically. Ti±15V±3Al, Ti±6Al±4V, and Ti±22Al±23Nb were chosen as matrix materials. The initiation and propagation of each individual matrix crack as a function of fatigue cycle...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2016
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.m2016216