Fatigue crack growth under mixed-mode I + II and I + III in heat treated 42CrMo4 steel
نویسندگان
چکیده
Abstract The paper contains the results of an experimental investigation fatigue crack development under mixed-mode I + II and III in heat-treated 42CrMo4 steel. Tests were performed on compact tension shear specimens rectangular cross-section for III. Mixed-mode tests conducted 30 60° loading angle, while test was 45°. Additionally, presents fracture analysis path development.
منابع مشابه
Finite Element Modeling of Crack Initiation Angle Under Mixed Mode (I/II) Fracture
Present study deals with the prediction of crack initiation angle for mixed mode (I/II) fracture using finite element techniques and J-Integral based approach. The FE code ANSYS is used to estimate the stress intensity factor numerically. The estimated values of SIF were incorporated into six different crack initiation angle criteria to predict the crack initiation angle. Single edge crack spec...
متن کاملPrediction of post overload fatigue crack growth life of HSLA steel under mixed-mode (I and II) spike overload by using genetic programming
In the present investigation, fatigue crack growth tests under mixed-mode (I and II) overload have been conducted on HSLA steel and subsequently genetic programming has been applied to predict post overload fatigue life. It is observed that the proposed model predicts fatigue life of HSLA steel with reasonable accuracy.
متن کاملThe Effect of Inclined U-Notch Geometry on Mode Ratio (KII/KI) under Mixed Mode (I + II) Loading
In inclined U-notches, the mixed mode (I + II) loading occurs and the mode ratio can be increased by varying the notch angle. In this paper, the effect of the inclined U-notch geometry, i.e. the notch depth, the notch angle, the notch root radius, and the position of the notch with respect to supports, on the mode ratio (KII/KI) have been studied. Three-point bending and plane strain condition ...
متن کاملShort and Large Crack , Mixed - Mode Fatigue - Crack Growth Thresholds in Ti - 6 Al - 4 V
There are few experimental results to date describing the crack-propagation threshold behavior of short fatigue cracks under multiaxial loading conditions. To address this need, in the present study, the variation in mixed-mode, high-cycle fatigue-crack growth thresholds with crack size and shape are reported for a Ti-6Al-4V turbine blade alloy, heat treated to two widely different microstructu...
متن کاملModelling Mode I Crack Initiation in Composites under Fatigue Loading Using Interface Elements
Modelling quasi-static crack growth with interface elements is a widely accepted technique [1-2]. Interface elements are inserted into the finite element mesh along possible crack paths. The interface elements are characterised by a traction-displacement curve. When a specific maximum stress is reached, the interface element undergoes a softening process until the critical fracture energy has b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Fracture
سال: 2021
ISSN: ['0376-9429', '1573-2673']
DOI: https://doi.org/10.1007/s10704-021-00585-0