Fatigue crack growth in thin aluminium alloy sheets under loading sequences with periodic overloads
نویسندگان
چکیده
منابع مشابه
Experimental Study of Sable Crack Growth in Thin Aluminium Sheet
Recent failure information from research teams in NASA Langley and others has shown that CTOA based fracture models calibrated on large C(T) and M(T) specimens can be transferred successfully to cracked aircraft fuselage structures for the assessment of their residual strength. A major difficulty that could limit the more extensive use of this failure parameter is its experimental measurement e...
متن کاملA New Probabilistic Approach for Describing Fatigue Crack Growth under Random Overloads
A new probabilistic model describing the fatigue crack growth with retardation due to random overloads is developed. First, a crack growth equation is formulated based upon the Flber law, where a concept of retardation factor is introduced to quantify the retardation effect. Next, a new approach is discussed for describing the temporal variation of the retardation factor by the use of a system ...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملFatigue crack growth in a coarse-grained iron–silicon alloy
The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...
متن کاملFatigue crack growth in ferroelectrics driven by cyclic electric loading
Fatigue crack growth has been observed recently in ferroelectrics under cyclic electric loading[ Does the crack grow by electric breakdown\ or by the stress _eld near the crack tip< The present paper provides a mechanistic explanation for the electric!_eld!induced fatigue crack growth[ The non!uniform electric _eld near an insulated crack tip might cause domain switching which in turn produces ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Thin-Walled Structures
سال: 2005
ISSN: 0263-8231
DOI: 10.1016/j.tws.2004.11.001