Fatigue crack growth in nodular cast iron – Influences of graphite spherical size and variable amplitude loading
نویسندگان
چکیده
منابع مشابه
Analyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملStrip yield modelling of fatigue crack under variable amplitude loading
The results from ‘strip yield’ approach of the FASTRAN type models of plasticity induced crack closure effects of fatigue cracks subjected to variable amplitude loadings are presented. The strip yield results are compared with authors’ finite element (FE) and experimental results. It has been observed that the strip yield model is seen to be fundamentally limited by choice of α (constraint fact...
متن کاملTransient Fatigue-crack Growth Behavior following Variable-amplitude Loading in a Monolithic Silicon Nitride Ceramic
ÐTransient cyclic fatigue-crack growth behavior following variable-amplitude loading sequences has been investigated in a hot-pressed, monolithic Si3N4 ceramic (NTK EC-141), for which fracture toughness (resistance-curve) and cyclic fatigue properties are well characterized. Following rapid changes in the applied stress-intensity range, DK, during both low-high and high-low block-loading sequen...
متن کاملFatigue Analyses Under Constant- and Variable-Amplitude Loading Using Small-Crack Theory
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملPrediction of Crack Growth under Variable-Amplitude Loading in Thin-Sheet 2024-T3 Aluminum Alloys
The present paper is concerned with the application of a “plasticity-induced” crack closure model to study fatigue crack growth under various load histories. The model was based on the Dugdale model but modified to leave plastically deformed material in the wake of the advancing crack. The model was used to correlate crack growth rates under constant-amplitude loading and then used to predict c...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2010
ISSN: 1742-6596
DOI: 10.1088/1742-6596/240/1/012060