Fatigue crack growth in 5083 aluminum alloy under varying loading conditions.
نویسندگان
چکیده
منابع مشابه
Crack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملAccelerated Threshold Fatigue Crack Growth Effect – Powder Metallurgy Aluminum Alloy
Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low ∆K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels...
متن کاملFatigue of polycrystalline silicon for microelectromechanical system applications: crack growth and stability under resonant loading conditions
Although bulk silicon is not known to exhibit susceptibility to cyclic fatigue, micron-scale structures made from silicon films are known to be vulnerable to degradation by fatigue in ambient air environments, a phenomenon that has been recently modeled in terms of a mechanism of sequential oxidation and stress-corrosion cracking of the native oxide layer. To date, most stress-life (S=N ) fatig...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملFatigue crack growth in a coarse-grained iron–silicon alloy
The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1992
ISSN: 0451-5994
DOI: 10.2464/jilm.42.45