Fatigue Crack and Cumulative Fatigue Damage of Notched Specimens

Prediction of Fatigue Life in Notched Specimens Using Multiaxial Fatigue Criteria

In this research, the effects of notch shape on the fatigue strength of 2024-T3 aluminum alloy notched specimens have been studied using experimental and multiaxial fatigue analysis. For this purpose, four set of specimens with different notch shape were prepared and then fatigue tests were carried out at various cyclic longitudinal load levels. Load controlled fatigue tests of mentioned specim...

Cumulative Fatigue Damage Under stepwise Tension-Compression Loading

Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...

Fatigue crack initiation in a notched single-crystal superalloy component

In this paper, the fatigue crack initiation in notched single-crystal test specimens of material MD2 is investigated and analysed. A critical plane approach is adopted, in which the total strain ranges on the discrete slip planes are evaluated. Furthermore, a Coffin-Manson type of expression is used to describe the number of cycles to fatigue crack initiation. This relation is determined from a...

Fatigue and Static Strength of Notched and Unnotched Aluminum-alloy and Steel Specimens

.This paper describes a method of presentation of fatigue da ta on three commonly ~ ~ s e d aircraft materials, 2024 '1'3 and 7075-'l'fi aluminurn ~ ~ l l o y s and normalized S;2E -ll:IO steel, suc.11 th;i t variations in f'atiguc: s t rength with siress-conc.enl~.niir)n factor can he shown. ( :on j):irisons of the fatigue sLrengt1-i~ o f 2024-'I':I anti 7075-'I'6 aluininiim are made for the m...

Thermomechanical Fatigue Life Prediction of Notched