Fatigue behaviour of 42CrMo4 steel under contact loading
نویسندگان
چکیده
منابع مشابه
Mechanical behaviour of TWIP steel under shear loading
Twinning induced plasticity steels (TWIP) are very good candidate for automotive industry applications because they potentially offer large energy absorption before failure due to their exceptional strain hardening capability and high strength. However, their behaviour is drastically influenced by the loading conditions. In this work, the mechanical behaviour of a TWIP steel sheet sample was in...
متن کاملBehaviour of Corroded Stud Shear Connectors under Fatigue Loading
Experimental investigation was conducted on corroded composite push-out specimens to study the behavior of shear studs subjected to fatigue loading. A total of eight standard EC4 push-out specimens were tested. The expected corrosion rate of test specimens ranged from 0 to 50%. The main purpose of these tests was to determine the fatigue life and the reduction effect caused by the corrosion on ...
متن کاملImpact Fatigue Behaviour of Flapper Valve Steel
The purpose of this study is to discuss the impact fatigue failure mechanism of a suction valve that involves the fracture with fragments torn off from the edge or surface. The shape and dimensions of the test specimen and stopper were made the same as those of the suction valve and stopper in an actual compressor. The specimen was operated by short-duration compressed air pulses, and struck ag...
متن کاملHigh Cycle Fatigue Property of Carburized 20Cr Gear Steel under Axial Loading
Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...
متن کاملFatigue strength evaluation of self-piercing riveted cold rolled steel joints under mixed mode loading conditions
Fatigue strength of cross-shaped specimens of SPR joints made of SPCC was evaluated at load angles of 0°, 45°, and 90°. For the static strength at load angles of 0°, 45°, and 90°, the maximum loads were determined to be 4890N, 1969N, and 1611N, respectively. Regarding for the relationship between the load amplitude and the number of cycles (Nf), the results were 014 . 0 3 . 2209 − = f amp N P ,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2010
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2010.03.214