Using magnetron sputtering and heat treatment, Ag@TiO2 nanotubes are prepared. The effects of heat-treatment temperature and heating time on the evolution of Ag nanofilms on the surface of TiO2 nanotubes and microstructure of Ag nanofilms are investigated by X-ray diffraction, field emission scanning electron microscopy, and transmission electron microscopy. Ag atoms migrate mainly on the outmo...
متن کاملSuper-long aligned TiO2/carbon nanotube arrays.
5 mm long aligned titanium oxide/carbon nanotube (TiO(2)/CNT) coaxial nanowire arrays have been prepared by electrochemically coating the constituent CNTs with a uniform layer of highly crystalline anatase TiO(2) nanoparticles. While the presence of the TiO(2) coating was confirmed by scanning electron microscopy, transmission electron microscopy, Raman spectroscopy and x-ray diffraction, the r...
متن کاملIdeally Hexagonally Ordered TiO2 Nanotube Arrays
Ideally hexagonally ordered TiO2 nanotube layers were produced through the optimized anodization of Ti substrates. The Ti substrates were firstly covered with a TiN protecting layer prepared through atomic layer deposition (ALD). Pre-texturing of the TiN-protected Ti substrate on an area of 20×20 μm2 was carried out by focused ion beam (FIB) milling, yielding uniform nanoholes with a hexagonal ...
متن کاملFast-rate formation of TiO2 nanotube arrays in an organic bath and their applications in photocatalysis.
In this work, 18.5 microm titanium oxide (TiO(2)) nanotube arrays were formed by the anodization of titanium (Ti) foil in ethylene glycol containing 1 wt% water and 5 wt% fluoride for 60 min at 60 V. The fast growth rate of the nanotube arrays at 308 nm min(-1) was achieved due to the excess fluoride content and the limited amount of water in ethylene glycol used for anodization. Limited water ...
متن کاملNanoindentation study of the mechanical behavior of TiO2 nanotube arrays
Articles you may be interested in The study of the mechanical properties of Au films by nanoindentation techniques AIP Conf. High magnetic field annealing effect on visible photoluminescence enhancement of TiO2 nanotube arrays Appl. Magnetic and mechanical properties of rolled-up Au/Co/Au nanomembranes with multiple windings Direct observation of twin deformation in YBa2Cu3O7− x thin films by i...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Beilstein Journal of Nanotechnology
سال: 2016
ISSN: 2190-4286
DOI: 10.3762/bjnano.7.105