FAILURE MICROMECHANISMS OF NODULAR CAST IRON
نویسندگان
چکیده
منابع مشابه
Failure Analysis of a Four Cylinder Diesel Engine Crankshaft Made From Nodular Cast Iron
The premature breakage in some four cylinder diesel engine crankshafts was reported. All crankshafts were failed from the same region. Failures had occurred in the first crankpin, the nearest crankpin to the flywheel. Dynamic analysis and finite element modelling were carried out to determine the state of stress in the crankshaft. FEM results revealed that the first crankpin fillet is the most ...
متن کاملPearlitic ductile cast iron: damaging micromechanisms at crack tip
Ductile cast irons (DCIs) are characterized by a wide range of mechanical properties, mainly depending on microstructural factors, as matrix microstructure (characterized by phases volume fraction, grains size and grain distribution), graphite nodules (characterized by size, shape, density and distribution) and defects presence (e.g., porosity, inclusions, etc.). Versatility and higher performa...
متن کاملfailure analysis of a four cylinder diesel engine crankshaft made from nodular cast iron
the premature breakage in some four cylinder diesel engine crankshafts was reported. all crankshafts were failed from the same region. failures had occurred in the first crankpin, the nearest crankpin to the flywheel. dynamic analysis and finite element modelling were carried out to determine the state of stress in the crankshaft. fem results revealed that the first crankpin fillet is the most ...
متن کاملCast iron component failure: A metallurgical investigation
A fractured nutcracker was examined for determining the root cause/s for premature fracture/failure. This is one of the common tools used typically for cracking hard nuts. In this study, metallurgical failure analysis techniques namely, visual inspection, optical microscopy, SEM, and hardness tests were used in investigating the broken product. From the metallurgical analysis, it was determined...
متن کاملModeling of Ultrasonic Testing for Inspection of Nodular Cast Iron Insert
Nodular cast iron insert will be used as the inner component of nuclear fuel disposal canister. The outer cover of the canister is copper tube of 50 mm nominal thickness. Nodular cast iron insert is cast around several steel channels, which also strengthen the structure. The mechanical properties of the cast iron insert will be tested according EN-1563 /1/. According the specifications 100% NDT...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Production Engineering Archives
سال: 2014
ISSN: 2353-5156,2353-7779
DOI: 10.30657/pea.2014.05.08