Failure investigation on high velocity impact deformation of boron carbide (B4C) reinforced fiber metal laminates of titanium / glass fiber reinforced polymer
نویسندگان
چکیده
منابع مشابه
An Investigation into the Deep Drawing of Fiber-Metal Laminates based on Glass Fiber Reinforced Polypropylene
Abstract Fiber-metal laminates (FMLs) are new type of composite materials which could improve defects of traditional composites in ductility, formability, impact and damage tolerance. Drawing behavior of a thermoplastic based FML was investigated consisting of glass-fiber reinforced polypropylene composite laminate and aluminum AA1200-O as the core and skin layers, respectively. The effects o...
متن کاملStrengthening of Corrosion-Damaged Reinforced Concrete Beams with Glass Fiber Reinforced Polymer Laminates
Problem statement: This study showed the results of an experimental investigation on the strengthening of corrosion damaged reinforced concrete beams with unidirectional cloth glass fiber reinforced polymer (UDCGFRP) laminates. Approach: All the beam specimens 150×250×3000 mm were cast and tested for the present investigation. One beam specimen was neither corroded nor strengthened to serve as ...
متن کاملExperimental Investigation of Behavior of Glass Fiber Reinforced Concrete (GFRC)
The paper presents the results of casting and testing of 264 GFRC specimens. The glass fibers were 25 mm long, with the aspect ratio (L/D) ranging between 1250 and 3570. The parameters studied were the ratio (by weight) of fibers to cement, i.e. F/C=0%, 1.5%, 3%, and 4.5%, and the ratio of coarse to fine aggregates (gravel to sand), i.e. G/S=1.1, 0.7 and 0.2. In total, 12 mix designs were selec...
متن کاملExperimental Investigation of Behavior of Glass Fiber Reinforced Concrete (GFRC)
The paper presents the results of casting and testing of 264 GFRC specimens. The glass fibers were 25 mm long, with the aspect ratio (L/D) ranging between 1250 and 3570. The parameters studied were the ratio (by weight) of fibers to cement, i.e. F/C=0%, 1.5%, 3%, and 4.5%, and the ratio of coarse to fine aggregates (gravel to sand), i.e. G/S=1.1, 0.7 and 0.2. In total, 12 mix designs were selec...
متن کاملWoven Glass Fiber-Reinforced
ment methods and two spec/imen diameters. Flexural strength and modulus of woven glass fiber-reinforced specimens werc significanLly greater than those without woven glass fiber (p<O.OD, Likewise, comprossive strength of reinforced specimens was signifieantly greater than those without woven glass fiber (p<O.Ol), except for specimens rcjnforced with woven glass fiber oriented at a tilt directio...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Defence Technology
سال: 2021
ISSN: 2214-9147
DOI: 10.1016/j.dt.2021.04.006