Failure investigation of a Kaplan turbine blade
نویسندگان
چکیده
منابع مشابه
Investigation of blade failure in a gas turbine
A gas turbine abruptly tripped to a stop during its daily morning start-up period. Out of a total of 81 blades in the first row only one blade was broken at its root. Prior to this accident, there were three blade failure accidents in the same plant during the last 10 years. First, the fracture surface of the troubled blade was investigated. Stress analysis of the blade showed that the maximum ...
متن کاملMetallurgical fatigue failure analysis of the brazed steam turbine blade
In this paper, failure mechanism of a 17th stage blade of an 82.5 MW steam turbine that caused damage to the internal turbine compartment and the adjacent blade equipment has been studied. In order to determine the cause of failure and prevent similar events, various metallurgical and mechanical investigations including chemical composition analysis, metallography and microstructural analysis, ...
متن کاملMetallurgical fatigue failure analysis of the brazed steam turbine blade
In this paper, failure mechanism of a 17th stage blade of an 82.5 MW steam turbine that caused damage to the internal turbine compartment and the adjacent blade equipment has been studied. In order to determine the cause of failure and prevent similar events, various metallurgical and mechanical investigations including chemical composition analysis, metallography and microstructural analysis, ...
متن کاملTurbine Blade Illusion
In January 2017, a large wind turbine blade was installed temporarily in a city square as a public artwork. At first sight, media photographs of the installation appeared to be fakes - the blade looks like it could not really be part of the scene. Close inspection of the object shows that its paradoxical visual appearance can be attributed to unconscious assumptions about object shape and light...
متن کاملAnalysis of the Fracture of a Turbine Blade
The cause of crack initiation turbine blade had initially cracked by a fatigue mechanism over a period of time and then fractured by the overload at the last moment. Experimental procedure consists of macroscopic inspection, material verification, microscopic examination, and metallographic analysis and finally FE. And for these procedures, some specimens were prepared from a fractured blade. Us...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Engineering Failure Analysis
سال: 2019
ISSN: 1350-6307
DOI: 10.1016/j.engfailanal.2019.01.056