Factors Affecting on Mechanical Properties of Soft Martensitic Stainless Steel Castings
نویسندگان
چکیده
منابع مشابه
Microstructure, Mechanical and Corrosion Properties of Friction Stir Welding High Nitrogen Martensitic Stainless Steel 30Cr15Mo1N
High nitrogen martensitic stainless steel 30Cr15Mo1N plates were successfully welded by friction stir welding (FSW) at a tool rotation speed of 300 rpm with a welding speed of 100 mm/min, using W-Re tool. The sound joint with no significant nitrogen loss was successfully produced. Microstructure, mechanical and corrosion properties of an FSW joint were investigated. The results suggest that the...
متن کاملElectrochemical Characterization of a Martensitic Stainless Steel
This paper focused on the characterization of electrochemical behavior of a martensitic stainless steel in the acidic solutions. For this purpose, electrochemical parameters were derived from potentiodynamic polarization, Mott Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that corrosion current density of AISI 420 ...
متن کاملFactors Affecting Friction Coating on Stainless Steel 304
Low carbon steels are widely used for structural applications because of its ease in fabrication and the moderate strength it posses. However, its pure corrosion resistance at normal atmosphere is a matter of serious concern.
متن کاملThe Effect of Tempering Treatment on the Microstructure and Mechanical Properties of DIN 1.4021 Martensitic Stainless Steel
To investigate the effect of tempering treatment on mechanical properties and the microstructure of DIN 1.4021 Martensitic Stainless Steel, austenite treatment was conducted for the samples at 1000 ºC temperature for 60 min and then the samples were oil quenched. Later, tempering treatments were performed for the samples at 500 ºC and 700 ºC temperatures for 2 and 5 h, respectively; then quench...
متن کاملThermoelectric Power Studies on a Martensitic Stainless Steel
In this work the different contributions to the thermoelectric power (TEP) measurement during the dissolution process of M23C6 carbides in an X45Cr13 stainless steel have been evaluated. Thus, the influences of carbon and chromium contents in solid solution in the austenite, the austenite grain boundaries and the microstructure on the TEP have been determined.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: JSME International Journal Series A
سال: 2003
ISSN: 1344-7912,1347-5363
DOI: 10.1299/jsmea.46.441