Facile synthesis of Cd-substituted zeolitic-imidazolate framework Cd-ZIF-8 and mixed-metal CdZn-ZIF-8
نویسندگان
چکیده
منابع مشابه
Porous Proton Exchange Membrane Based Zeolitic Imidazolate Framework-8 (ZIF-8)
Metal-organic frameworks (MOFs) are emerging material class for the past few years due to its tailorability characteristics for various applications. However, the research and development (R&D) of MOFs is still scarce for fuel cell system. This may be due to the several difficulties faced in selecting a good MOFs-based electrolyte, which consequently affects both proton conduction and methanol ...
متن کاملRapid synthesis of zeolitic imidazolate framework-8 (ZIF-8) nanocrystals in an aqueous system.
We report here the first example of ZIF materials synthesized in aqueous solution. The synthesis was performed at room temperature and typically took several minutes compared to hours and days in non-aqueous conditions. The obtained product were ZIF-8 nanocrystals having size of ~85 nm and showed excellent thermal, hydrothermal and solvothermal stabilities.
متن کاملOpening ZIF-8: a catalytically active zeolitic imidazolate framework of sodalite topology with unsubstituted linkers.
A zeolitic imidazolate framework material of SOD topology possessing primarily unsubstituted imidazolate (im) linkers has been synthesized via solvent-assisted linker exchange (SALE) of ZIF-8. The structure of the new material, SALEM-2, has been confirmed through (1)H NMR and powder and single-crystal X-ray diffraction. SALEM-2 is the first example of a porous Zn(im)(2) ZIF possessing a truly z...
متن کاملImmobilization of lysozyme proteins on a hierarchical zeolitic imidazolate framework (ZIF-8).
A hierarchical zeolitic imidazolate framework-8 (micro/meso-ZIF-8) was fabricated by using cetyltrimethylammonium bromide as a structure-controlling agent and l-histidine as co-templates. Compared to the conventional microporous ZIF-8 (micro-ZIF-8), the hierarchical porous structure of micro/meso-ZIF-8 contains micropores and maximum mesopores of around 35.6 nm. The as-prepared hierarchical mic...
متن کاملAmorphization of the prototypical zeolitic imidazolate framework ZIF-8 by ball-milling.
We report the rapid amorphization of the prototypical substituted zeolitic imidazolate framework, ZIF-8, by ball-milling. The resultant amorphous ZIF-8 (a(m)ZIF-8) possesses a continuous random network (CRN) topology with a higher density and a lower porosity than its crystalline counterpart. A decrease in thermal stability upon amorphization is also evident.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microporous and Mesoporous Materials
سال: 2018
ISSN: 1387-1811
DOI: 10.1016/j.micromeso.2017.12.032