Fabrication of Wood-Rubber Composites Using Rubber Compound as a Bonding Agent Instead of Adhesives
نویسندگان
چکیده
منابع مشابه
Fabrication of Wood-Rubber Composites Using Rubber Compound as a Bonding Agent Instead of Adhesives
Differing from the hot-pressing method in the manufacturing of traditional wood-rubber composites (WRCs), this study was aimed at fabricating WRCs using rubber processing to improve water resistance and mechanical properties. Three steps were used to make WRCs, namely, fiber-rubber mixing, tabletting, and the vulcanization molding process. Ninety-six WRC panels were made with wood fiber content...
متن کاملProduction method of rubber and sulfur FG composites
In the presented work, sulfur concrete and rubber were used for producing functionally graded materials (FGM). The physical and mechanical properties of sulfur concrete and rubber were changed continuously across the thickness. On one side, there was just rubber and, on the other, there was pure sulfur; the properties of each substance were moved to reach another. This kind of material was cons...
متن کاملMaize Stalk As Reinforcement In Natural Rubber Composites
Maize stalk fibres can be used as fillers in natural rubber composites replacing expensive and non-biodegradable inorganic fillers. Maize stalk fibres were chemically modified with acetic anhydride (acetylation) to enhance their compatibility with the hydrophobic rubber polymer matrix. The fibre was characterised using FTIR showing a spectrum with a well defined peak at 1742 cm -1 (attributed t...
متن کاملEffect of silanes as crosslinking agent with the NBR rubber
Silane coupling agent generally use as improve the properties of white filler use in rubber compound for better dispersion. Also silane coupling agent reacts with organic filler & polymer chain as crosslink. Here in this research study the crosslink density & swelling phenomena of silane participate in vulcanization process with Nitrile rubber compound. Also show the comparisons of carbon fille...
متن کاملHigh Performance Graphene Oxide Based Rubber Composites
In this paper, graphene oxide/styrene-butadiene rubber (GO/SBR) composites with complete exfoliation of GO sheets were prepared by aqueous-phase mixing of GO colloid with SBR latex and a small loading of butadiene-styrene-vinyl-pyridine rubber (VPR) latex, followed by their co-coagulation. During co-coagulation, VPR not only plays a key role in the prevention of aggregation of GO sheets but als...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2016
ISSN: 1996-1944
DOI: 10.3390/ma9060469