Fabrication of transparent lead-free KNN glass ceramics by incorporation method
نویسندگان
چکیده
منابع مشابه
Fabrication of transparent lead-free KNN glass ceramics by incorporation method
The incorporation method was employed to produce potassium sodium niobate [KNN] (K0.5Na0.5NbO3) glass ceramics from the KNN-SiO2 system. This incorporation method combines a simple mixed-oxide technique for producing KNN powder and a conventional melt-quenching technique to form the resulting glass. KNN was calcined at 800°C and subsequently mixed with SiO2 in the KNN:SiO2 ratio of 75:25 (mol%)...
متن کاملMicrostructure of Transparent Strontium Fresnoite Glass-Ceramics
Glass-ceramics grown from a glass of the composition Sr2TiSi2.45O8.9 (STS 45) are analyzed by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Oriented nucleation with the c-axes preferably perpendicular to the surface is detected. A very strong 001-texture is observed after only 10 μm of growth into the bulk, making this the first system in which an orientation p...
متن کاملProcessing of transparent glass-ceramics by nanocrystallisation of LaF3
ransparent glass-ceramics have been prepared by heat-treating oxyfluoride glasses in the Na2O–Al2O3–SiO2–LaF3 system. The nanocrystallisation f LaF3 was achieved by controlling time and temperature parameters. Glasses and glass-ceramics were characterised by dilatometry, DTA, XRD nd TEM. The mean crystal size (<20 nm) and the crystal fraction increase with the temperature of heat treatment, whi...
متن کاملNanoparticles and Fabrication of Transparent Polycrystalline Yttria Ceramics
In this thesis, we report on a process to obtain yttrium oxide nanosized particles doped with ytterbium and a sintering method that leads to transparent polycrystalline ceramics. First, nano-powder of yttria was fabricated from a precursor with transient morphology, i.d. yttrium hydroxynitrate platelets that decompose into spherical yttria nano-particles during calcination. The influence of dif...
متن کاملFabrication of Na2FeP2O7 glass-ceramics for sodium ion battery
New cathode candidate Na2FeP2O7 for rechargeable sodium ion second battery was successfully prepared by glass-ceramics method. The precursor glass, which is same composition in Na2FeP2O7, was prepared by melt-quenching method. Na2FeP2O7 was obtained by heat treatment of precursor glass powder with 10% glucose addition as reduction agent of Fe3+ at 620°C for 3 h in electric furnace. Na2FeP2O7 ha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2012
ISSN: 1556-276X
DOI: 10.1186/1556-276x-7-136