Fabrication of Thin YSZ Electrolyte Films Using Spray Pyrolysis Technique

Fabrication and characterization of fluorine-doped thin oxide thin films and nanorod arrays via spray pyrolysis

This paper reports the synthesis and characterization of fluorine-doped tin oxide (FTO) thin films via intermittent spray pyrolysis utilizing a solution mixture of tin chloride pentahydrate and ammonia fluoride. Utilizing the same solution, nanorod arrays were fabricated via template-based growth. Uniform and crack-free FTO films over 20×20 mm with a thickness up to 900 nm have been routinely a...

Cadmium Oxide Thin Films Deposited by a Simplified Spray Pyrolysis Technique for Optoelectronic Applications

Cadmium oxide thin films were fabricated on glass substrates by a simplified and low cost spray pyrolysis technique at different substrate temperatures. The X-ray diffraction study showed that irrespective of substrate temperature all the films exhibits a preferential orientation along the (1 1 1) plane. The values of crystallite size were found to be in the range 20.72 – 29.6 nm. The perce...

Fabrication and Characterizations of YSZ Electrolyte Films for SOFC

Yttria stabilized zirconia (YSZ) has been widely used as electrolyte in solid oxide fuel cell (SOFC). The effect of fabrication process on the properties of YSZ electrolyte thick film is discussed in the paper. With YSZ nano-powders of about 20-60nm as raw material, YSZ green adobe was fabricated by tape calendering process. Three-step sintering process was performed firstly holding at 1000°C f...

The growth of CuS thin films by Spray Pyrolysis

Thin films of CuS (covellite) were deposited onto TCO (SnO2:F) glass by Spray Pyrolysis (SP) technique. Aqueous and water:alcohol (ethanol, 1-propanol) solutions of copper(II) chloride and thiourea with different Cu/S molar ratio have been used as precursors. The substrate temperature was varied from 185°C to 285°C. The structural and the morphological characterization of the films has been car...

cadmium oxide thin films deposited by a simplified spray pyrolysis technique for optoelectronic applications