Fabrication of MoSi 2 Base Heating Element by Slip Casting Process
نویسندگان
چکیده
منابع مشابه
Fabrication of high–strength alumina composite foams through gel–casting process
A water–soluble gelatin combined with polyethylene microspheres were developed to prepare alumina composite foam. Gelatin was used as the gelling agent and polyethylene was used as pore making template. On the other hand, kaolin was used to provide green strength and CuO was applied to decrease the required temperature as a sinter aid. Alumina bodies need elevate temperature for sintering, incr...
متن کاملFabrication of Saddle-Shaped Surfaces by Flame Forming Process
The flame forming process is widely used to manufacture ship hull plates. The saddle-shaped surfaces have different curvatures in perpendicular angles of planes and the manufacturers face an anti-clastic curvature. In this article, the manufacturing of saddle-shaped surfaces utilizing the flame forming process is investigated. The spiral irradiating scheme is used for forming. In order to study...
متن کاملIN-SITU FABRICATION PROCESS OF AL- TIC COMPOSITE BY SLAG
The new in situ method for AI-TiC composite fabrication has been carried out. In this method, fabrication of AI-TiC composite by simultaneous introduction of titanium oxide and carbon into aluminum melt was investigated.. Under the process conditions, titanium and carbon reaction results in titanium carbide whiskers. The salt containing keriolite (Na3AIF6), titanium oxide (TiO2) and graphite us...
متن کاملFabrication and Characterization of Porous MgAl2O4 Ceramics via a Novel Aqueous Gel-Casting Process
A novel and aqueous gel-casting process has been successfully developed to fabricate porous MgAl₂O₄ ceramics by using hydratable alumina and MgO powders as raw materials and deionized water as hydration agent. The effects of different amounts of deionized water on the hydration properties, apparent porosity, bulk density, microstructure, pore size distribution and compressive strength of the sa...
متن کاملfabrication of high–strength alumina composite foams through gel–casting process
a water–soluble gelatin combined with polyethylene microspheres were developed to prepare alumina composite foam. gelatin was used as the gelling agent and polyethylene was used as pore making template. on the other hand, kaolin was used to provide green strength and cuo was applied to decrease the required temperature as a sinter aid. alumina bodies need elevate temperature for sintering, incr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1963
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.10.44