Fabrication of Fe-Al nanoparticles by selective oxidation of Fe-Al thin films
The possibility of a new technique for fabricating nanoparticles from thin films using selective oxidation in an atmosphere mixture of water vapor and hydrogen was investigated. Fe-5wt.%Al films were RF-sputtered and annealed in the atmosphere mixture at 900°C for up to 200 min, in order to oxidize aluminum selectively. Thermodynamics simulation showed that temperatures exceeding 800°C are nece...
متن کاملMicrostructural evolution in Al–Cu–Fe quasicrystalline thin films
Transmission electron microscopy (TEM) was performed to study the microstructural evolution in Al–Cu–Fe quasicrystalline thin films. Thin films were grown by magnetron sputtering on sodium chloride crystals, which were subsequently dissolved in water to acquire free-standing films. Studies were conducted on the as-deposited sample, and samples that were annealed at 400 8C in Argon and 500 8C in...
متن کاملRoom Temperature Oxidation of Al-Cu-Fe and Al-Cu-Fe-Cr Quasicrystals
We have investigated formation of oxides on quasicrystalline and crystalline alloy surfaces of similar composition, in different oxidizing environments. This includes a comparison between a quaternary orthorhombic approximate of Al-Cu-Fe-Cr quasicrystal and the ternary AI-Cu-Fe quasicrystalline and crystalline phases. We noted that each sample showed the following common trends: preferential ox...
متن کاملThin Al, Au, Cu, Ni, Fe, and Ta films as oxidation barriers for Co in air
We have investigated the effectiveness of Al, Au, Cu, Ni, Fe, and Ta films with thicknesses up to 4 nm for protecting a Co surface from oxidation in air at room temperature. The distinct change in the Co 2p3/2 core-level line shape observed by x-ray photoelectron spectroscopy upon the oxidation of Co makes it a simple matter to identify the fractions of the Co that are in the metallic state and...
متن کاملFabrication of Fe-Cr-Al Oxide Dispersion Strengthened PM2000 alloy using Selective Laser Melting**
The expansion in application of the selective laser melting (SLM) process for fabrication of new alloy materials continues. However, to date, there has been no investigation of the effect of this process on the final microstructure of ‘melt sensitive’ powder alloys such as mechanically alloyed oxide dispersion strengthened (ODS) FeCrAl. In this study commercial PM2000 powder, a ferritic ODS all...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2013
ISSN: 1556-276X
DOI: 10.1186/1556-276x-8-152