Fabrication of Fe-Al Intermetallic Foams via Organic Compounds Assisted Sintering
The influence of the addition of organic compounds, such as palmitic acid and cholesteryl myristate, on the porous structure of Fe-Al intermetallics formation has been investigated in detail in this paper. It was found that additives have a significant effect on the final porosity of the obtained sinters. Formed gaseous products from combustion play the role of the foaming agent during Fe-Al in...
متن کاملAn Investigation of the Use of Ni3Al Intermetallic Compound for Fabrication of Al Matrix Composites
Fabrication and characterization of aluminum matrix composites containing different volume fractions of Ni3Al powder (5-40 Vol%) were investigated. Ni3Al powder was produced by mechanical alloying of elemental nickel and aluminum powder mixture. Al-Ni3Al composite parts were prepared using a powder metallurgy route involving two stages Al and Ni3Al powder mixtures were first compacted under 500...
متن کاملFabrication of Fe-Al nanoparticles by selective oxidation of Fe-Al thin films
The possibility of a new technique for fabricating nanoparticles from thin films using selective oxidation in an atmosphere mixture of water vapor and hydrogen was investigated. Fe-5wt.%Al films were RF-sputtered and annealed in the atmosphere mixture at 900°C for up to 200 min, in order to oxidize aluminum selectively. Thermodynamics simulation showed that temperatures exceeding 800°C are nece...
متن کاملAmino Acids Aided Sintering for the Formation of Highly Porous FeAl Intermetallic Alloys
Fabrication of metallic foams by sintering metal powders mixed with thermally degradable compounds is of interest for numerous applications. Compounds releasing gaseous nitrogen, minimizing interactions between the formed gases and metallic foam by diluting other combustion products, were applied. Cysteine and phenylalanine, were used as gas releasing agents during the sintering of elemental Fe...
متن کاملMicrowave-Assisted Sintering of Al–ZrO2 Nano-Composites
Abstract In this project, nano-ZrO2 particles were dispersed in aluminum powder by a Y-shape mixer. The particle size of ZrO2 powder was < 40 nm and the amount of ZrO2 reinforcement varies from 3 to 15%.The mixed powders were compacted .Subsequently the compacted discs were sintered both in the microwave oven and in the conventional muffle furnace .Using microwave –assisted sintering method led...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2015
ISSN: 1996-1944
DOI: 10.3390/ma8052217